Influence of H-Bonding on the Crystalline Structures, Ferroelectric and Piezoelectric Properties of Novel Nanogenerators of Lithium Salt of 6-Amino Hexanoic Acid Incorporated Poly(vinylidene fluoride) Composites

Ananya Aishwarya,Akanksha Adaval,Suvankar Mondal,Titas Dasgupta,Arup Bhattacharyya
DOI: https://doi.org/10.1039/d4cp02497d
IF: 3.3
2024-10-06
Physical Chemistry Chemical Physics
Abstract:Lithium salt of 6-amino hexanoic acid (Li-AHA) was melt-mixed with poly(vinylidene fluoride) (PVDF), wherein Li-AHA concentration was varied between 1-15 wt.% with an aim to establish H-bonding between NH2 functionality of Li-AHA and the -CF2 moieties of PVDF. This was followed by compression-moulding as well as solution-casting to make PVDF/Li-AHA composite thin films. FTIR analysis established interactions between -CF2 groups in PVDF with amine functional moieties of Li-AHA. Moreover, FTIR analysis estimated that solution-casted PVDF/Li-AHA composite of 15 wt.% Li-AHA exhibited highest polar phase fraction of ~ 60%. Furthermore, ferroelectric analysis showed that solution-casted PVDF/Li-AHA composite of 15 wt.% Li-AHA exhibited highest remnant polarization of 0.07 μC/cm2 (at 50 Hz, 1000 V) from polarization versus electric field loop. Finally, energy harvester devices were fabricated with compression-moulded as well as solution-casted PVDF/Li-AHA composite films, in which a maximum output voltage of ∼ 110 V was obtained in solution-casted PVDF/Li-AHA composite of 15 wt.% Li-AHA. The devices also displayed a maximum power density of 75 μW/cm2 and 85 μW/cm2, which was fabricated via compression-moulding and solution-casting, respectively. Three different capacitors were efficiently charged by the tapping of the devices made from solution-casted and compression-moulded composite films of 15 wt.% Li-AHA. An interrelation between processing, structure and property was successfully established in PVDF/Li-AHA composites with greatly enhanced piezoelectric properties.
chemistry, physical,physics, atomic, molecular & chemical
What problem does this paper attempt to address?