Research on mechanism change of temperature effect on dephosphorization in the bottom-blown O 2 -CaO process of semi-steelmaking
Chunyang Wang,Rong Zhu,Kai Dong,Guangsheng Wei,Xin Ren,Yun Zhou,Zhitao Xue,Chao Feng
DOI: https://doi.org/10.1016/j.jmrt.2023.05.113
IF: 6.267
2023-05-17
Journal of Materials Research and Technology
Abstract:In semi-steelmaking, the bottom-blown O 2 -CaO process is employed to achieve high efficiency dephosphorization. However, there is little research on the requirements for smelting parameters. In this paper, the mechanism changes of temperature effect on dephosphorization is studied by the industrial tests in a 300 t dephosphorization converter. Initially, the influences of temperature on equilibrium constant ( K P ), CaO melting ratio ( K ) and slag viscosity ( ƞ ) were analyzed. K P decreases, K increases and ƞ decreases to stability with increasing temperature. The dephosphorization effect is better than the conventional process' even at higher ƞ , because of the CaO powder has molten and P is mostly removed during the process of fire-spot zone upward floatation Hence, the requirements for slagging with good fluidity reduce. Then, the relationships between the three factors and phosphorus partition between slag and hot metal ( L P ) were investigated by the correlation analysis. The importance order in the bottom-blown O 2 -CaO process is: lg K P > η , it demonstrates that the melting of CaO powder doesn't affect dephosphorization. While the influence order in the conventional process is: K > η >lg K P . Finally, we summarize the dephosphorization reaction in the bottom-blown O 2 -CaO process includes transient reaction accounts for approximately 86% and continuous reaction with about 14%. The process of CaO upward floatation plays major roles on dephosphorization. Based on above results, the temperature requirements of molten steel for dephosphorization become lower. The industrial tests showing the optimum temperature range for dephosphorization decreases from 1593-1603 K to 1573-1583 K, which validate the conclusion.
materials science, multidisciplinary,metallurgy & metallurgical engineering