Effect of Layer Thickness and Heat Treatment on Microstructure and Mechanical Properties of Alloy 625 Manufactured by Electron Beam Powder Bed Fusion
Julio Cesar Diaz,Kurtis Watanabe,Aldo Rubio,Alex De La Cruz,Dana Godinez,Shadman T. Nabil,Lawrence E. Murr,Ryan B. Wicker,Edel Arrieta,Francisco Medina
DOI: https://doi.org/10.3390/ma15217767
IF: 3.4
2022-11-04
Materials
Abstract:This research program investigated the effects of layer thickness (50 μm and 100 μm) on the microstructure and mechanical properties of electron beam powder bed fusion (EBPBF) additive manufacturing of Inconel 625 alloy. The as-built 50 μm and 100 μm layer thickness components were also heat treated at temperatures above 1100 °C which produced a recrystallized grain structure containing annealing twins in the 50 μm layer thickness components, and a duplex grain structure consisting of islands of very small equiaxed grains dispersed in a recrystallized, large-grain structure containing annealing twins. The heat-treated components of the microstructures and mechanical properties were compared with the as-built components in both the build direction (vertical) and perpendicular (horizontal) to the build direction. Vickers microindentation hardness (HV) values for the vertical and horizontal geometries averaged 227 and 220 for the as-built 50 μm and 100 μm layer components, respectively, and 185 and 282 for the corresponding heat-treated components. The yield stress values were 387 MPa and 365 MPa for the as-built horizontal and vertical 50 μm layer geometries, and 330 MPa and 340 MPa for the as-built 100 μm layer components. For the heat-treated 50 μm components, the yield stress values were 340 and 321 MPa for the horizontal and vertical geometries, and 581 and 489 MPa for the 100 μm layer components, respectively. The elongation for the 100 μm layer as-built horizontal components was 28% in contrast with 65% for the corresponding 100 μm heat-treated layer components, an increase of 132% for the duplex grain structure.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering