Abstract:This study investigates the mechanical, electrochemical and microstructural characteristics of UHPC bonded cementitious composite systems concerning the influences of chloride attack. The bonded composite systems with styrene-butadiene rubber (SBR) latex content of 0, 2 %, 4 %, 6 %, 8 % in UHPC layers were prepared. The experimental groups were immersed in saturated sodium chloride solution whereas the reference groups were cured in clean water. The compressive, bonding and flexural strength of the bonded systems were tested at different curing ages. The free corrosion potential, AC impedance spectroscopy and polarization resistance were considered to figure out their electrochemical behaviors. Furthermore, X-ray diffraction (XRD), pore structure characteristics as well as scanning electron microscope (SEM) observations were employed to show some light on the internal mechanism at a microscale level. Results indicate that the chloride-rich environment demonstrated certain adverse effects on the system's mechanical properties, especially the bonding strength, which could be reduced by 20 % on average at 56d. Proper content of SBR latex was conducive to the system's bonding strength. However, when the dosage was too large, a remarkable adverse effect on compressive strength was seen. The addition of SBR latex could further delay the corrosion of the reinforcement inside the system, from 28d of the systems without latex to 42d with 4 % SBR latex. The microstructural investigations confirmed that in a chloriderich environment, the total pore volume was reduced by 29.4 % at 28d. A dense transition zone was observed between the substrate and the UHPC layer with a width of about 0.1 mu m in clean water curing, whereas it became relatively loose and obvious bonding holes appeared in this area under severe chloride attack.

Synergistic effects of sustained loading and sulfate attack on the damage of UHPC based on lightweight aggregate

Sulphate attack resistance of high-performance concrete under compressive loading

Performances of UHPC Bonded Cementitious Composite Systems Containing Styrene-Butadiene Rubber Latex in a Chloride-Rich Environment

Investigation of the damage of L-HPC under stress corrosion

Sulfate resistance of ultra-high performance concrete with recycled fine aggregate

Concrete Deterioration Mechanisms under Combined Sulfate Attack and Flexural Loading

Assessment of Mechanical Properties and Damage of High Performance Concrete Subjected to Magnesium Sulfate Environment

Enhancing Sulfate Erosion Resistance in Ultra-High-Performance Concrete through Mix Design Optimization Using the Modified Andreasen and Andersen Method

Combined effects of sulfate attack under drying–wetting cycles and loading on the fatigue behavior of concrete

Analysis of High Performance Concrete Mixed with Nano-Silica in Front of Sulfate Attack

Deterioration Mechanisms of Ultra-High-Performance Concrete Under Various Sulfuric Acid and Sulfate Attack Conditions

The Synergistic Effects of Ultrafine Slag Powder and Limestone on the Rheology Behavior, Microstructure, and Fractal Features of Ultra-High Performance Concrete (UHPC)

Study on dynamic properties of lightweight ultra-high performance concrete (L-UHPC)

Experimental investigation and reliability prediction of high performance concrete based on lightweight aggregate under 4-point bending loading

Mechanical properties and microstructure of ultra-high strength concrete with lightweight aggregate

Effect of sulfate attack on multiple interfacial transition zones of high-belite sulfoaluminate cement recycled concrete

Durability of micro-cracked UHPC subjected to coupled freeze-thaw and chloride salt attacks

Use of saturated lightweight sand to improve the mechanical and microstructural properties of UHPC with fiber alignment

The damage evolution behavior of polypropylene fiber reinforced concrete subjected to sulfate attack based on acoustic emission

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Sulphate Corrosion Mechanism of Ultra-High-Performance Concrete (UHPC) Prepared with Seawater and Sea Sand