Polyatomic self-doping millet-derived porous carbon for supercapacitor
Ru Li,Qian Zhang,Yude Zhang,Jiebin Wang,Yan Li,Rongjun Gao,Yuanyuan Li,Baimei Zhang
DOI: https://doi.org/10.1016/j.diamond.2024.111250
IF: 3.806
2024-05-30
Diamond and Related Materials
Abstract:The selecting of supercapacitor electrode materials, has seen a growing interest in biomass-derived carbon materials due to their surface functional groups and unique pore structure. In this study millet-derived porous carbon (MIC-PxRy) with heteroatoms including nitrogen (N), oxygen (O), phosphorous (P), and sulfur (S) was synthesized through a successive pre‐carbonization and chemical activation process. The structure and distribution of heteroatoms in the MIC-PxRy were effectively controlled by adjusting the pre‐carbonization and activation temperatures. When the pre‐carbonization and activation temperatures are both at 600 °C, the resulting sample (MIC-P6R6) exhibited a high specific surface area (1798.79 m 2 g −1 ) was co-doped with oxygen atoms (10.77 %), nitrogen atoms (1.40 %), sulfur atoms (0.76 %) and phosphorus atoms (0.26 %). In a three-electrode system, the MIC-P6R6 demonstrated a specific capacitance of 458.6 Fg −1 at 1 A g −1 , which remained stable at 336.2 F g −1 even under higher current densities up to 20 A g −1 . In a two-electrode system with KOH electrolyte, it exhibited an impressive specific capacitance of 314.2 F g −1 along with an energy density of 10.91 Wh kg −1 (at 250 W kg −1 , 1 A g −1 ). Furthermore, after undergoing durable 20,000 cycling tests (at 5 A g −1 ), the MIC-R6A6 demonstrated exceptional capacitance retention rate of 92.1 %. This study provides a novel self-doped activated carbon material with multiple heteroatoms at a lower activation temperature, which can improve the performance of symmetric supercapacitors.
materials science, multidisciplinary,physics, applied, condensed matter, coatings & films