Abstract:Porous carbon materials, characterized by variable surface morphologies, pore structures, crystallinity, and corresponding mechanisms for ion and electron storage and transport, are one of the promising electrode materials for supercapacitors. In this study, ammonium alginate, phenolic resin and calcium ions were introduced to form a nanoscale semi-interpenetrating network structure by sol-gel method. Further, porous carbon materials were prepared through carbonization and KOH activation. By adjusting the activation temperature and alkalito-carbon ratio, the activation rules and electrochemical properties of the porous carbon were obtained. Eventually, a coral-like three-dimensional (3D) porous carbon with high specific surface area was constructed. The alkali-to-carbon ratio and the activation temperature can influence the specific surface area. When the alkalito-carbon ratio was 1:4 and the activation temperature was 800 C-degrees, the activated carbon material used as supercapacitor electrode material achieved the highest specific capacitance in an aqueous electrolyte. Moreover, the capacitive performance of a two-electrode capacitor using an organic system as the electrolyte was investigated, and the specific capacitance reached 125.1 F/g at a current density of 0.5 A/g. The carbon material showed good cycling stability in the organic supercapacitor, maintaining >94 % of the initial specific capacitance in a voltage window of 0-2.5 V for 10,000 cycles. This investigation provides a reference for the construction of high-performance 3D hierarchical carbon materials for supercapacitors.

Rational construction of hierarchical porous carbon with ultrahigh specific surface area and rich heteroatoms toward high-performance supercapacitors

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

N, S Co-doped hierarchical porous carbon rods derived from protic salt: Facile synthesis for high energy density supercapacitors

Facile synthesis of chitosan derived heteroatoms-doped hierarchical porous carbon for supercapacitors

Facile synthesis of heteroatom-doped hierarchical porous carbon with small mesopores for high-performance supercapacitors

Boosting the capacitive performance by constructing O, N co-doped hierarchical porous structure in carbon for supercapacitor

Fabrication of high performance structural N-doped hierarchical porous carbon for supercapacitors

N, O self-codoped hierarchical porous carbon from chitosan for supercapacitor electrode active materials

3D nitrogen and sulfur co-doped hierarchical porous carbon derived from mung bean jelly for high performance supercapacitors

Fabrication of N/O self-doped hierarchical porous carbons derived from modified coal tar pitch for high-performance supercapacitors

Three-dimensional Nitrogen-Doped Hierarchical Porous Carbon Derived from Cross-Linked Lignin Derivatives for High Performance Supercapacitors

Thiocyanogen-modulated N, S Co-doped lignin hierarchical porous carbons for high-performance aqueous supercapacitors

Biomass-derived nitrogen-doped porous carbons with tailored hierarchical porosity and high specific surface area for high energy and power density supercapacitors

Facile and low-cost fabrication of interconnected hierarchically porous carbon for high-performance supercapacitors

Rational Fabrication of Semi-Interpenetrating Three-Dimensional Hierarchical Carbon Materials for High-Performance Symmetric Supercapacitor

An in-situ Blowing-etching strategy for preparation of Macro-meso-micro hierarchical porous carbon and its supercapacitive property

Chitin derived nitrogen-doped porous carbons with ultrahigh specific surface area and tailored hierarchical porosity for high performance supercapacitors

Nitrogen and Phosphorus Co-doped Porous Carbon for High-Performance Supercapacitors

Multi-heteroatom-doped Hierarchical Porous Carbon Derived from Chestnut Shell with Superior Performance in Supercapacitors

Heteroatoms co-doped multi-level porous carbon as electrode material for supercapacitors with ultra-long cycle life and high energy density

Boosting capacitive performance of N, S co-doped hierarchical porous lignin-derived carbon via self-assembly assisted template-coupled activation