Ultrafast Synthesis of MXenes in Minutes via Low‐Temperature Molten Salt Etching
Yongbin Wang,Bin Zhou,Qi Tang,Yi Yang,Ben Pu,Jia Bai,Jing Xu,Qingguo Feng,Yan Liu,Weiqing Yang
DOI: https://doi.org/10.1002/adma.202410736
IF: 29.4
2024-10-19
Advanced Materials
Abstract:MXenes, including Ti3C2Tx, V4C3Tx, Nb4C3Tx, Mo2TiC2Tx, and Mo2CTx, can be rapidly synthesized via the low‐temperature (130–195 °C) NH4HF2 molten salt etching process from their corresponding MAX phases in just 5–40 min. This low‐temperature molten salt etching method is easy to scale up and can yield more than 100 g MXene in a single reaction. Developing green and efficient preparation strategies is a persistent pursuit in the field of 2D transition metal nitrides and/or carbides (MXenes). Traditional etching methods, such as HF‐based or high‐temperature Lewis‐acid‐molten‐salt etching route, require harsher etching conditions and exhibit lower preparation efficiency with limited scalability, severely constraining their commercial production and practical application. Here, an ultrafast low‐temperature molten salt (LTMS) etching method is presented for the large‐scale synthesis of diverse MXenes within minutes by employing NH4HF2 as the etchant. The increased thermal motion and improved diffusion of molten NH4HF2 molecules significantly expedite the etching process of MAX phases, thus achieving the preparation of Ti3C2Tx MXene in just 5 minutes. The universality of the LTMS method renders it a valuable approach for the rapid synthesis of various MXenes, including V4C3Tx, Nb4C3Tx, Mo2TiC2Tx, and Mo2CTx. The LTMS method is easy to scale up and can yield more than 100 g Ti3C2Tx in a single reaction. The obtained LTMS‐MXene exhibits excellent electrochemical performance for supercapacitors, evidently proving the effectiveness of the LTMS method. This work provides an ultrafast, universal, and scalable LTMS etching method for the large‐scale commercial production of MXenes.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology