Abstract:Microwave (MW) treatment was reported as an efficient method to prepare porous carbon-based electrode material with high capacity for a high-performance supercapacitor. Herein, the superiority of the mechanism of MW treatment was tried to be revealed by preparing a N and O co-doped porous activated carbon (MWAC) based on a heteroatom-rich corn cob and compared to that of the conventional heating method. The resulting MWAC has a large specific surface area of 2508 m<sup>2</sup>/g with hierarchical micro- and mesoporous structures and abundant heteroatom doping of O and N. In a three-electrode system, the MWAC shows a superior specific capacitance of 560 F/g at a discharge current density of 0.5 A/g in a 6 mol/L KOH aqueous electrolyte. The symmetric supercapacitor fabricated by MWAC electrodes in a 6 mol/L KOH electrolyte shows excellent capacity retention of 96.8%, even after 10 000 galvanostatic charge–discharge cycles at the current density of 1 A/g. The aqueous (6 mol/L KOH) symmetric supercapacitor delivers a high energy density of 9.24 Wh/kg at a power density of 250 W/kg. The results prove that the MW heating shows more superiority in retaining inherent heteroatoms and creating hierarchical micro- and mesoporous structures of activated carbon for supercapacitors with high performance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00337?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00337</a>.Systematic condition optimization experiments for the preparation of MWAC, including MW power, activation time, and mass ratio of C/KOH (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00337/suppl_file/ef1c00337_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Hydrothermal preparation of N and O-rich porous carbon microspheres and their capacitance properties

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Highly N/O co-doped ultramicroporous carbons derived from nonporous metal-organic framework for high performance supercapacitors

Highly Active N, O-doped Hierarchical Porous Carbons for High-Energy Supercapacitors

Highly graphitized porous carbon microspheres derived from copolymer of glucose and melamine for advanced electrodes

Soluble starch-derived porous carbon microspheres with interconnected and hierarchical structure by a low dosage KOH activation for ultrahigh rate supercapacitors

Glucose-derived activated carbons for supercapacitors: comparison between single O doping and N/O co-doping

From weed to N/O/S co-doped honeycomb-like porous carbon for high-performance supercapacitors: a facile and friendly one-step carbonization

Preparation of N/O co-doped porous carbon by a one-step activation method for supercapacitor electrode materials

Microwave-Assisted Preparation of Hierarchical N and O Co-Doped Corn-Cob-Derived Activated Carbon for a High-Performance Supercapacitor

Deep insight into the pore size distribution of N-doped porous carbon materials on electrochemical energy storage and CO2 sorption

Porous Carbon Spheres Derived from Hemicelluloses for Supercapacitor Application

Nitrogen-doped micro-nano carbon spheres with multi-scale pore structure obtained from interpenetrating polymer networks for electrochemical capacitors

Nitrogen-doped highly dense but porous carbon microspheres with ultrahigh volumetric capacitance and rate capability for supercapacitors

Chitin derived nitrogen-doped porous carbons with ultrahigh specific surface area and tailored hierarchical porosity for high performance supercapacitors

Impregnation Assisted Synthesis of 3d Nitrogen-Doped Porous Carbon with High Capacitance

Oriented and Interlinked Porous Carbon Nanosheets with an Extraordinary Capacitive Performance

Synthesis of activated carbon nanospheres with hierarchical porous structure for high volumetric performance supercapacitors

Preparation of biomass-based N, P, and S co-doped porous carbon with high mesoporosity based on the synergistic effect of NaOH/thiourea and melamine phosphate and its application in high performance supercapacitors

N/P co-doped porous carbon microspheres for supercapacitor with long-term electrochemical stability

Biomass derived N/O self-doped porous carbon for advanced supercapacitor electrodes