Abstract:The greatest challenge in the subsequent processing of alumina ceramic slit arrays is the strength of the cutting wall. Because of its high brittleness, the fracture toughness of the wall has become one of the most important factors limiting the cutting quality. In the process of laser cutting alumina ceramics, α-γ reverse phase transformation is caused by the lattice dislocation effect due to instantaneous impact of high-energy beam, which can be induced in the heating/melting process and retained in the rapid cooling process. Generally speaking, due to the metastable characteristics of γ-Al2O3 lattice structure, the density, hardness and mechanical strength of the phase change products are obviously lower than α-Al2O3. However, the looser structure endows γ-Al2O3 with higher shear deformation component and fracture toughness, which potentially generates self-reinforcing effect when attached to the substrate. By controlling the material removal mode, i.e. vapor-to-melt ratio, the effects of different phase transformation content and distribution on the wall of slit array is discussed to reveal the phenomenon and mechanism of α-γ phase transformation self-reinforcing. The results show that the thickness of phase transformation layer and mass fraction of γ-Al2O3 both decrease with the increase of rvmr and the existence of phase transformation layer will slightly reduce the Vickers hardness of residual molten layer. However, a thinner phase transformation layer can simultaneously enhance the fracture toughness of the slit wall. Through the observation of the micromorphology and the comprehensive evaluation of the mechanical properties of the slit wall, it can be concluded that, under the appropriate vapor-to-melt ratio parameters (stable state of the molten layer and good cutting quality), the material is removed in time, and a small amount of phase transformation products contained in the residual molten layer can produce a self-reinforcing effect on the cutting slit.

A novel method by microwave cutting ceramics based on thermal crack and trajectory control

Tailored microwave thermal crack heating model and its application in cutting ceramics

Thermal Controlled Fracture of Al2O3 Substrate by Inducing Microwave Discharge in Graphite Coat

Microwave thermal stress method cutting Al2O3 ceramics: modeling and experiments

Mechanism Of Irregular Crack-Propagation In Thermal Controlled Fracture Of Ceramics Induced By Microwave

Understanding the Processing Quality Problem for Cutting Ceramic Materials Using the Thermal-Controlled Fracture Method Induced by a Single-Surface Heat Source

Simulation and analysis of laser-controlled thermal stress cutting of alumina ceramic

A Simple Method for Predicting the Machinability in Microwave Cutting Ceramics with Microwave-Induced Thermal-Crack Propagation

Splitting Opaque, Brittle Materials with Dual-Sided Thermal Stress Using Thermal-Controlled Fracture Method by Microwave

Numerical analysis of laser-controlled thermal stress cutting of an alumina ceramic

Theoretical and Experimental Investigation on Inclined Ultrasonic Elliptical Vibration Cutting of Alumina Ceramics

Use of inner-heated circular microwave spot to cut glass sheets based on thermal-controlled fracture method

Crack Arrest in Brittle Ceramics Subjected to Thermal Shock and Ablation

Research Progress of Thermal Controlled Cracking of Hard-Brittle Plate

Alpha-to-gamma phase transformation self-reinforcing of Alumina Ceramic Slit Array in Nd:YAG Laser Cutting Based on Vapor-to-melt Ratio Controlling

On Crack Suppression Mechanisms of Ultrasonic Elliptical Vibration Cutting of 3Y-TZP Ceramics

Kinetic research of oxidation induced crack healing of engineering ceramics (III) model testing and revising: The kinetic research of Al2O3-SiCW composite

Effect of Technological Parameters on Laser-Controlled Thermal Stress Cutting Quality of Ceramics

Fractal characterization of ceramic crack patterns after thermal shocks

Effect of process parameters on crack characteristics in laser welding of Al2O3 ceramic

Multiscale Finite Element Modeling of Alumina Ceramics Undergoing Laser-Assisted Machining