Abstract:Homogeneous mesoporous lignocellulose aerogels were prepared from hardwood using 1-allyl-3-methylimidazolium chloride (AMImCl) as an ionic liquid (IL) via cyclic liquid nitrogen freezing-thawing (NFT, from -196 degrees C to 20 degrees C) treatment processes. The obtained hydrogels after NFT treatment were solvent-exchanged by acetone, washed with liquid carbon dioxide and then dried by releasing the carbon dioxide at the critical temperature. It was observed that the obtained aerogels after five-cycles of NFT treatment had open-structured 3-dimensional (3D) fibril-like networks. The surface areas and pore size distributions could be adjusted by controlling the NFT treatment cycles. However, the samples treated by common freezing-thawing (FT, from -20 degrees C to 20 degrees C) displayed a film-like 2D structure and low surface area. This may be ascribed to the difference of the assembled 'secondary units' formed during the freezing process. For instance, in the NFT process, 3D-like 'secondary assembly units' were squeezed out by small IL crystals formed during the ultra low temperature freezing process. These 'secondary assembly units' were able to build a large 3D network through the connection and overlap effect with cyclic NFT processes. However, the assembled 2D-like 'secondary assembly units' were squeezed out by large IL crystals in the common FT process due to the slow freezing process and finally were developed to a film-like structure. These 'secondary assembly units' could be linked together in a slow thawing process to form compact aerogels. This study provides a new means to fabricate novel mesoporous lignocellulose aerogels, which is crucial to fully utilize abundant lignocellulose biomass. The homogeneous mesoporous aerogels can be used as highly insulating materials with low thermal conductivity and also have appealing performance in sound absorption and noise reduction properties.

Strong, Shape-Memory Lignocellulosic Aerogel via Wood Cell Wall Nanoscale Reassembly

Nanostructurally Controllable Strong Wood Aerogel toward Efficient Thermal Insulation

Top-Down Approach Making Anisotropic Cellulose Aerogels As Universal Substrates for Multifunctionalization

"Rigid-Flexible" Anisotropic Biomass-Derived Aerogels with Superior Mechanical Properties for Oil Recovery and Thermal Insulation

Rigid and Fire-Resistant All-Biomass Aerogels

Ultralight Biomass Aerogels with Multifunctionality and Superelasticity Under Extreme Conditions

Strong, Lightweight, and Shape-Memory Bamboo-Derived All-Cellulose Aerogels for Versatile Scaffolds of Sustainable Multifunctional Materials

Water-assisted synthesis of phenolic aerogel with superior compression and thermal insulation performance enabled by thick-united nano-structure

Shaping 90 wt% NanoMOFs into Robust Multifunctional Aerogels Using Tailored Bio-Based Nanofibrils

Fully biomass-based aerogels with ultrahigh mechanical modulus, enhanced flame retardancy, and great thermal insulation applications

Biomimetic, hierarchical-ordered cellulose nanoclaw hybrid aerogel with high strength and thermal insulation

Preparation and Investigation of High Surface Area Aerogels from Crosslinked Polypropylenes

Lightweight, ultrahigh-strength and flame-retardant cellulose aerogel crosslinked with a reactive P/N-rich curdlan derivative

Cross-Linked and Shapeable Porous 3D Substrates from Freeze-Linked Cellulose Nanofibrils

Robust Carbonaceous Nanofiber Aerogels from All Biomass Precursors

Carbonized clay pectin-based aerogel for light-to-heat conversion and energy storage

Double cross-linked biomass aerogels with enhanced mechanical strength and flame retardancy for construction thermal insulation

Structure and performance preparation on alginate-based fibrous aerogel with double network

Double-cross-linked aerogels towards ultrahigh mechanical properties and thermal insulation at extreme environment

Fabrication of Mesoporous Lignocellulose Aerogels from Wood Via Cyclic Liquid Nitrogen Freezing–thawing in Ionic Liquid Solution

Monolithic carbon aerogels within foam framework for high-temperature thermal insulation and organics absorption