Abstract:In the present research, microstructure, texture, roughness, hardness, and electrochemical behavior of AISI 316L austenitic stainless steel before and after shot peening were studied to elucidate the effect of conventional and severe shot peening (CSP and SSP) processes. After the shot peening, the fraction of strain-induced martensite (SIM) and mechanical twins (MTs) in the sub-surface layer was increased. The fraction of SIM and MTs in the SSP sample was higher than in the CSP sample. The XRD patterns indicated that the SSP sample had a higher peak broadening compared to the CSP sample. In the CSP and SSP samples, a gradient microstructure was formed along the depth direction. The microstructure of the topmost layer of the CSP and SSP samples exhibited numerous ultrafine grains. The grain refining during severe shot peening was faster because of the accumulation of more strain. The CSP and SSP samples revealed a gradient distribution of elements. After the SSP, the intensity of ⟨110⟩‖ED fiber texture decreased from 12.7 to 11.6 × R and the average intensity of ⟨100⟩‖ED fiber texture increased from 1.7 to 2.0 × R, respectively, compared to the CSP sample. The surface roughness of the SSP sample (Rq = 73.6 nm and Ra = 45.2 nm) was lower than that of the CSP sample which represented the roughness decreased with surface coverage increasing from 100 % to 1500 %. Also, the wettability increased after the conventional and severe shot peening processes. In addition, the microhardness of the CSP and SSP samples showed a gradient distribution. The CSP sample had the lowest corrosion current density (0.13 μA/cm2) whereas the NP (non-peened) sample exhibited the highest current density (0.65 μA/cm2). The presence of ⟨100⟩-oriented grains in both CSP and SSP samples led to the higher corrosion resistance of shot-peened steels compared to the NP sample. The presence of favorable texture with higher intensity in the CSP sample was responsible for the higher corrosion resistance of the CSP sample compared to the SSP sample. Finally, the gradient distribution of elements along the depth direction in the CSP and SSP steels improved the corrosion resistance of the surface.

Effect of shot peening strengths on microstructure and mechanical properties of 316L stainless steel prepared by 3D printing

Effect of Shot Peening Duration on Microstructure and Mechanical Properties of GH4169 Alloy Prepared by 3D Printing

Effect of Micro-Shot Peening on the Fatigue Performance of AISI 304 Stainless Steel

Revealing the relationship between the shot type and fatigue performance of laser powder bed fused 304L steel following shot peening

Shot peening coverage effect on laser powder bed fused steel

Surface Nanocrystallization Mechanism of Additive Manufactured 316L Stainless Steel Via High-Energy Shot Peening

Effect of ultrasonic shot peening on microstructure and properties of 301SS

The Effect of Severe Shot Peening on Fatigue Life of Laser Powder Bed Fusion Manufactured 316L Stainless Steel

Evaluation of 3D printed 316L stainless steel microstructure and mechanical property by laser ultrasonics

Effect of shot peening on surface characteristics and high-temperature corrosion behaviour of super 13Cr martensitic stainless steel

Corrosion resistance of 3D printed SS316L post-processed by ultrasonic shot peening at optimum energy level

The effects of laser peening on laser additive manufactured 316L steel

Tribological behavior and surface characteristics of severe surface plastic deformed as-cast and 3D-printed SS316L using LSP

On the effect of small laser spot size on the mechanical behaviour of 316L stainless steel fabricated by L-PBF additive manufacturing

Comparison of conventional and severe shot peening effects on the microstructure, texture, roughness, hardness, and electrochemical behavior of austenitic stainless steel

3D-printed metals: Process parameters effects on mechanical properties of 17-4 P H stainless steel

Ultrasonic shot peening of 316L stainless steel – Experimental and analytical approach

Laser powder bed fused 304L steel shot-peened with various ceramic shot sizes: Surface/subsurface characteristics, tensile behavior, and fatigue behavior

Characterization of Surface Modification of 347 Stainless Steel Upon Shot Peening

Effect of Severe Shot Peening on Mechanical Properties and Fatigue Resistance of Wire Arc Additive Manufactured AISI 316L

Influence of initial relative densities on the sintering behavior and mechanical behavior of 316 L stainless steel fabricated by binder jet 3D printing