Inorganic porous carbon as the supporter of H 2 TiO 3 via in-situ polymerization synchronous conversion for lithium recovery from aqueous solutions

Junmin Wu,Wenxing Wang,Wenzhe Chen,Can Liu,Tianlong Deng,Xiaoping Yu

DOI: https://doi.org/10.1016/j.seppur.2024.129806

IF: 8.6

2024-09-26

Separation and Purification Technology

Abstract:The extraction of lithium from liquid minerals, such as salt lake brines and underground brines, has garnered extensive interest due to its eco-friendly and cost-effective properties. However, the effectiveness of this method is constrained by the stability and capacity of the materials. Herein, a new-type inorganic carbon-supported H 2 TiO 3 adsorbent was developed by a novel in-situ polymerization synchronous conversion strategy. It was found that when resorcinol and formaldehyde containing Li 2 CO 3 and TiO 2 were polymerized in-situ and then calcined at 973.15 K, the resin was successfully carbonized to obtain the carbon supporter with a low degree of disorder, and the Li 2 CO 3 and TiO 2 in the supporter were synchronously converted into Li 2 TiO 3 and uniformly dispersed in the carbon matrix. Because of the large specific surface area and strong hydrophilicity of the carbon supporter, the material exhibited a maximum Li + adsorption capacity of 52.14 mg·g −1 , which was far higher than that of inorganic composite materials reported at present. Even the equilibrium adsorption capacity for Li + at a low concentration of 29.26 mg·L −1 reached 28.51 mg·g −1 . Following adsorption, the Li + in the material was easily eluted by 0.25 mol·L −1 HCl, and the elution rate was more than 90 % within 2 h. Dynamic adsorption using a fixed-bed was also performed at 298.15 and 343.15 K, and the adsorption capacity for the same concentration of Li + was 7.08 and 9.44 mg·g −1 , respectively. Because of the high capacity for low-concentration Li + and the promoting effect of temperature on adsorption, the material is well-suited for recovering Li + from liquid resources, particularly from geothermal water with high temperatures and low Li + concentrations.

engineering, chemical