Abstract:Tensile and flexural performance of carbon‐fiber epoxy composites with carbon fibers electrophoretically coated with carboxyl graphene and their failure mechanisms. Polymer composites reinforced with carbon fiber (CF) are strong, light weight and corrosion‐resistant, and have a wide range of applications in automobile, sports, aerospace, wind energy etc. but are prone to fail at the interface of epoxy and fiber due to weak interfacial adhesion between the fiber and epoxy. Formation of an interphase region with a continuous gradation of properties between fiber and the epoxy can potentially delay failure. Development of a larger interphase can be facilitated by the inclusion of graphene platelets on carbon fiber surface through various deposition processes. The present investigation utilizes a unique combination of magnesium nitrate hexahydrate and carboxyl graphene (G‐COOH) to create a colloidal solution for the particulate type deposition of G‐COOH onto carbon fibers through electrophoretic deposition (EPD). Four layers of EPD deposited carbon fibers have been used to make the composite using vacuum assisted resin transfer molding technique. Tensile and flexural tests have been conducted on the pristine and 0.45 wt% of G‐COOH deposited carbon fiber (0.45G‐COOH CF) epoxy composite. G‐COOH addition leads to thickening of the interphase which has been confirmed through energy‐dispersive x‐ray spectroscopy line scanning. The tensile and flexural strength properties of the carboxyl graphene deposited composites exhibited an increase of 62% and 12% respectively. These improvements can be ascribed to the deposition of carboxyl graphene particles on the fiber and an enhancement in interphase thickness. Moreover, the addition of G‐COOH in composites resulted in a 38% increase in tensile strain. The interlaminar shear strength (ILSS) and void content measured in 0.45G‐COOH CF have been compared with pristine carbon fiber composite as well as 1.3 wt% of carboxyl graphene (1.3G‐COOH) deposited carbon fiber fabric composite that had a film type morphology of G‐COOH deposition. There is only a slight decrease in ILSS of 0.45G‐COOH carbon fiber composites occurred compared to pristine carbon fiber composites. The film type morphology of carbon fiber composite showed the highest void content and lowest ILSS compared to other composites. The fracture surfaces of the failed composites were thoroughly examined through scanning electron microscope and they showed that the failure mechanisms in both tension and flexural loading were severely affected by the presence of G‐COOH. Highlights Optimization of electrophoretic deposition process parameters for carboxyl graphene deposition on carbon fiber fabrics. Enhancement composite strength through the particle type deposition of carboxyl graphene over film type deposition. Evaluation of the tensile, flexural and interlaminar shear strength of particle type carboxyl graphene deposited composite. Identified the failure mechanisms of these tests.

Compressive Failure of Polymer Composites Based on Graphene-Coated Particles

Influence of an Ultralow Graphene Content on the Physical and Mechanical Characteristics of UHMWPE-Based Composites

Effect of graphene nano-platelets on the low-velocity-impact and compression-after-impact strength of the glass fiber epoxy composite laminates

Molecular dynamics simulation of tension of polymer composites reinforced with graphene and graphene oxide

An unexpected hardening behaviour of carbon-fiber epoxy composites under flexural fatigue loading and its intensification by graphene nano-fillers

Water-Immersion Effect On Radial Crack Initiation Behavior In A Fiber-Bundle-Reinforced Epoxy Cylinder With Graphene In The Interfacial Region

Influence of hybrid nano/micro particles on the mechanical performance of cross-ply carbon fibre fabric reinforced epoxy polymer composite materials

Tensile and flexural strength enhancement in carbon‐fiber epoxy composites using a novel method of particle type electrophoretic deposition of carboxyl functionalized graphene on carbon fiber

Degradation and Breakdown of Polymer/Graphene Composites under Strong Electric Field

Mechanical Performance of Hybrid Graphene Nanoplates, Fly-Ash, Cement, Silica, and Sand Particles Filled Cross-Ply Carbon Fibre Woven Fabric Reinforced Epoxy Polymer Composites Beam and Column

Experimental and multiscale quantum mechanics modeling of the mechanical properties of PVC/graphene nanocomposite

Mechanical and thermal properties of rigid PVC and graphene nanocomposites obtained by melt–mixing

Drop-weight impact and compressive behavior of graphene-based carbon fiber-reinforced polymer composites

Is Graphene Always Effective in Reinforcing Composites? The Case of Highly Graphene-Modified Thermoplastic Nanofibers and Their Unfortunate Application in CFRP Laminates

Exploring the material and dielectric properties of poly(vinylidene fluoride) composites incorporated with graphene and graphene oxide

Non-Eulerian behavior of graphitic materials under compression

Graphene-based composite materials

Mechanical, thermal, and dynamic compression of high-density polyethylene nanocomposites with graphene, montmorillonite, and calcium carbonate

Graphene-based polymer composite films with enhanced mechanical properties and ultra-high in-plane thermal conductivity

Fatigue Behavior of Polymer Encapsulated Graphene to Mitigate Interfacial Fatigue Damage

Graphene-based high-performance pseudo-ductile glass-carbon/epoxy composites