Grain Refinement of CoNiCrMo Non-equiatomic Medium Entropy Alloy

DOI: https://doi.org/10.1007/s12540-022-01217-5

IF: 3.451

2022-06-02

Metals and Materials International

Abstract:Using a thermal–mechanical process, the average grain size of Co 35 Ni 34 Cr 24 Mo 7 medium entropy alloy was reduced to 2 μm, resulted in 50% improvement of hardness. In this way, the kinetic of the recrystallization and grain growth were investigated by annealing at the temperature range of 800–950 °C. Based on Differential Scanning Calorimetry analysis and microstructural investigations, recrystallization began around 800 °C at prior grain boundaries, micro shear bands, and intersected deformation marking. Comparing Johnson–Mehl–Avrami–Kolmogorov and Austin-Ricket approaches for recrystallization modeling the, revealed that the latter is more accurate considering its basic theory, which involves reducing recrystallization rate by impingement. Both recrystallization and grain growth activation energy were calculated around 380 kJ/mol, which is close to the activation energy of self-diffusion of similar high/medium entropy alloys. The recrystallization and grain growth time exponent were found to be less than 0.5, which indicates the heterogeneous deformation and recrystallization in structure and pining effect of Mo on the grain boundaries migration. It was observed that the annealed microstructure contains annealing twins, which their number and thickness are related to the recrystallized grain size. Moreover, it was revealed that due to the presence of annealing twins, the modified Hall–Petch equation with effective grain size is more appropriate to explain the relation of grain size and hardness.

materials science, multidisciplinary,metallurgy & metallurgical engineering