Abstract:Mesophase pitch precursor fibers are oxidized to various weight percentage increases and temperatures using in situ thermal analysis measurements. Fibers are then carbonized and tested for tensile mechanical performance. The best mechanical performance occurs at 5% oxidation, which differs from previous reports. However, the optimal oxidation point is not a universal number, but rather dependent on intrinsic material/processing parameters. Carbon fiber precursor materials, such as polyacrylonitrile, pitch, and cellulose/rayon, require thermal stabilization to maintain structural integrity during conversion into carbon fiber. Thermal stabilization mitigates undesirable decomposition and liquification of the fibers during the carbonization process. Generally, the thermal stabilization of mesophase pitch consists of the attachment of oxygen‐containing functional groups onto the polymeric structure. In this study, the oxidation of mesophase pitch precursor fibers at various weight percentage increases (1, 3.5, 5, 7.5 wt%) and temperatures (260, 280, 290 °C) using in situ differential scanning calorimetry and thermogravimetric analysis is investigated. The results are analyzed to determine the effect of temperature and weight percentage increase on the stabilization process of the fibers, and the fibers are subsequently carbonized and tested for tensile mechanical performance. The findings provide insight into the relationship between stabilization conditions, fiber microstructure, and mechanical properties of the resulting carbon fibers.

Fractal structure change of pitch-based carbon fiber during high-temperature heat treatment

High temperature in-situ synchrotron-based XRD study on the crystal structure evolution of C/C composite impregnated by FLiNaK molten salt

Study of Microstructure Evolution and Mechanical Behaviour Changes of PAN-based Carbon Fibers after High-Temperature Heat Treatment (up to 2950 °C)

In Situ Saxs Study Of Fractal Structure Of Non-Caking Coal During Carbonisation

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Effect of Heating Rate on Morphology and Structure of Cofe2o4 Nanofibers

In Situ Change of Fractal Structure in Coal with Coking Capability During High-Temperature Carbonisation

Influence of Elevated Temperature Treatment on the Microstructures and Mechanical Properties of Carbon Fibers in Argon Environment

Temperature-structure-induced metastable structural transformation mechanism of the amorphous carbon film during friction

Dependence of structures and properties of carbon nanotube fibers on heating treatment

Unveiling the microcrystal structure evolution of carbon fibers induced by thermal soaking of mesophase pitch

Small angle X-ray scattering from voids within fibers during the stabilization and carbonization stages

Microstructure of high thermal conductivity mesophase pitch-based carbon fibers

Assessment of the anisotropy development of mechanical properties of pitch-based carbon fibers

Thermal Aging Behavior of Carbon Fiber/Epoxy Composites at High Temperature

Mechanical Behavior of carbon felt-carbon composites under ultra-high temperature

Evolution of microstructures and thermal properties with heat treatment for absorbing, emitting and scattering fibrous medium

Influence of Oxygen Uptake on Pitch Carbon Fiber

In Situ Wide-Angle X-ray Scattering Study on the Change of Microcrystalline Structure in Jincheng Anthracite During High-Temperature Carbonization

Elucidation of Elemental and Structural Changes in High-Volatile Bituminous Coal During Thermal Treatment by X-ray Diffraction and Terahertz Time-Domain Spectroscopy

Improving the mechanical properties and thermal conductivity of mesophase-pitch-based carbon fibers by controlling the temperature in industrial spinning equipment