Abstract:Copper oxide was synthesis by hydrothermal method using copper nano powder (30nm) and deionized water on quartz substrate. At temperature 100 °C, different experimental time ranging from (24–72 h). Different copper oxide phase was presented in X-Ray diffraction analyzer, the crystal size increased as the reaction time increased as it calculated using scherrer equation to be (21.1–32.03 nm), and Williamson Hall plot to be (40.3–87.7 nm). Also, Raman spectroscopy show different copper phase and the highest intensity peak at 220 cm −1 , due to the cuprous oxide in all sample used to distinct chemical fingerprint for a particular molecule or material. Many of metal oxide bond was study by FTIR to clarify the compositional and chemical properties of the prepared samples. Optical characteristic with different absorption peaks of thin film show decrease in the band gap from (2.8–2.4 eV) as the reaction time increase. PL measurement used also to determine the band gap energy of the prepared thin film which found to be agreement with UV–Vis, and the band gap value is (2.7, 2.6, 2.5, 2.3, and 2.3 eV), respectively. Increasing in the surface roughness from (3.637–25.16 nm), and in the root mean square from (5–29.39 nm), and grain size with increasing the reaction time from (24–72 h), respectively, was measured by using AFM technique. Different morphologies were showed with increasing the reaction time, spherical and truncated octahedral in different type was obtained by field emission-scanning electron microscope (FE-SEM) as the particles subject to transformation caused the preparing agglomerated crystallites. The electrical characteristic was analysis use DC measurement to measure the activation energy which varied with reaction time. The figure of merit analysis shows that the copper oxidation state to obtain cuprous oxide (Cu 2 O) is mainly obtained at the 48 h-reaction time. The used of copper nano powder in hydrothermal method without adding any auxiliary material the main aim of this research.

Influence Different Substrates on the Sensing Performance of Copper Oxide Thin Films Synthesis via the Hydrothermal Method

Influence of Interphase Distribution of Reactants on Preparation of Nano-CuO by Adsorption Phase Technique

Electrochemical Synthesis and the Gas-Sensing Properties of the Cu2o Nanofilms/Porous Silicon Hybrid Structure

Deposition time effect on copper oxide nano structures, an analysis study using chemical method

Synthesis and characterization of Cu-Doped ZnO nanostructures for UV sensing application

Effect of Growth Temperature and Time on Morphology and Gas Sensitivity of Cu2O/Cu Microstructures

Synthesis of flower-like CuO nanostructures as a sensitive sensor for catalysis

Synthesis and Characterizations of Cu Doped Co3O4 Nanostructured Thin Films Using Spray Pyrolysis for Glucose Sensor Applications

Hydrothermal synthesis of hierarchically flower-like CuO nanostructures with porous nanosheets for excellent H2S sensing

Preparation, characterization, and morphology insight of ZnO nanodisk–TiO2‐coated SWCNT thin film composites for catalytic sensor application

Facile wet chemical synthesis of Al doped CuO nanoleaves for carbon monoxide gas sensor applications

Improvement of ozone sensing parameters by CuO–SnO2: F mixed oxide sprayed thin films

In situ synthesis of Cu2O nano/microstructures on a copper substrate assisted with mixed cationic/anionic surfactants

Effect of substrate surface treatment on the hydrothermal synthesis of zinc oxide nanostructures

Free-Standing Copper Oxide Films with in Situ Tailorable Nanostructures Toward Detection of Hydrogen Peroxide

Enhanced sensing performance of zinc oxide porous silicon heterojunction-based gas sensors

Facile synthesis of copper oxide nanostructures and their application in non-enzymatic hydrogen peroxide sensing

High sensitivity and fast response at the room temperature of SnO2:CuO/PSi nanostructures sandwich configuration NH3 gas sensor

Performance of high sensitive heterojunction CuS/porous silicon photodetector

One-step Synthesis of Ni-Mn-Al-O Thin Film on Al2O3 Substrate Via Hydrothermal Method

Temperature and time dependent morphological evolution of solution phase synthesized copper oxide nanostructures