Abstract:In this study, homogeneous (Ti, Nb)(C, B)/IN625 composite coatings with almost defect-free microstructures were successfully prepared on a 42CrMo steel substrate by coupling ultra-high-speed laser cladding (USLC) with the direct reaction synthesis (DRS) technique to introduce the in-situ exothermic reaction into the cladding materials; these were comparatively analyzed with the pure IN625 coating prepared only by USLC. Our results showed that the interface of the composite coating/substrate was greatly affected by about 670 kJ Joule heat released from the in-situ reaction happening during the cladding process, which was sufficient to remelt the as-deposited materials and significantly increased the coating/substrate interface width to around 24 μm, six times the interface width of pure IN625 coating. Furthermore, the residual stress inside the coating and across the interfacial region was also reduced, alleviating the interface stress mismatch. However, the surface hardness of (Ti, Nb)(C, B)/IN625 composite coating was found to be lower than that of the IN625 coating, and the average wear weight loss was only 10% of that of the IN625 coating, attributable to the in-situ authigenic TiCB, TiC, NbMo3B4 and NbMo2B2 phases providing load transfer from the hard phases to the IN625 composite matrix to achieve abrasion reduction and wear resistance. It was also found that the formation of nano-equiaxial ultrafine grains in the depth range of 250 nm below the wear surface was facilitated by the coupling of the three fields of plastic rheology-heat-force, which dynamically strengthened the wear surface. Based on these findings, it is suggested to promote the strategy of combing USLC and DRS techniques to achieve an additional ability to enhance the coating microstructure and reduce residual stress, to achieve better tribological performance.

Microstructural evolution and high-temperature oxidation of TiC/IN625 coatings fabricated by multi-layer extreme high-speed laser cladding

Effect of surface morphology and microstructure on the hot corrosion behavior of TiC/IN625 coatings prepared by extreme high-speed laser cladding

Improved Microstructure and Wear Resistance of (cocrni)82al9ti9 Cladding Layers Via Extreme High-Speed Laser Cladding

Effect of TiC addition on the microstructure and properties of laser cladding Ni60A coatings on H13 steel surface

Microstructure, Tribocorrosion and Corrosion Performances of Laser Cladded Ni625-xTiC Coatings in 3.5% NaCl Solution

Effect of multiple thermal cycling on the microstructure and microhardness of Inconel 625 by high-speed laser cladding

Effect of scanning speed on microstructure and properties of TiC/Ni60 composite coatings on Ti6Al4V alloy by laser cladding

Microstructure and properties of Ti–Al–C composite coatings prepared by laser cladding

Microstructure, thermostability and tribological behavior of composite CoCrFeNiTix high-entropy alloy coatings fabricated by laser cladding

Effect of the Laser Cladding Parameters on Microstructure and Elevated Temperature Wear of FeCrNiTiZr Coatings

Effects of TiC on the Microstructure, Mechanical Properties, and Wear Behavior of E690 Steel Prepared by Laser Cladding

Effect of Co/TiAl on Mechanical Properties of Laser Melted IN 625 on 304SS Matrix

Effect of Laser Scanning Speed on Microstructure and Wear Properties of T15M Cladding Coating Fabricated by Laser Cladding Technology

Microstructure regulation and performance of titanium alloy coating with Ni interlayer on the surface of mild steel by laser cladding

Microstructure and wear resistance of laser-clad Ni60-Ti-B4C coatings

Study on fabrication of multi-phase reinforcement coatings on Ti6Al4V by laser cladding for enhanced tribological performance

High-temperature oxidation behavior and corrosion resistance of in-situ TiC and Mo reinforced AlCoCrFeNi-based high entropy alloy coatings by laser cladding

Microstructure and wear properties of TiCN/Ti coatings on titanium alloy by laser cladding

Microstructures and Properties of Laser Cladding Al-TiC-CeO₂ Composite Coatings

A Comparative Study on Microstructure and Properties of Ultra-High-Speed Laser Cladding and Traditional Laser Cladding of Inconel625 Coatings

(Ti, Nb)(C, B)/IN625 In-Situ Reactive Coating Prepared by Ultra-High-Speed Laser Cladding: Interfacial Characterization, Residual Stress and Surface Wear Mechanisms