Abstract:In this study, homogeneous (Ti, Nb)(C, B)/IN625 composite coatings with almost defect-free microstructures were successfully prepared on a 42CrMo steel substrate by coupling ultra-high-speed laser cladding (USLC) with the direct reaction synthesis (DRS) technique to introduce the in-situ exothermic reaction into the cladding materials; these were comparatively analyzed with the pure IN625 coating prepared only by USLC. Our results showed that the interface of the composite coating/substrate was greatly affected by about 670 kJ Joule heat released from the in-situ reaction happening during the cladding process, which was sufficient to remelt the as-deposited materials and significantly increased the coating/substrate interface width to around 24 μm, six times the interface width of pure IN625 coating. Furthermore, the residual stress inside the coating and across the interfacial region was also reduced, alleviating the interface stress mismatch. However, the surface hardness of (Ti, Nb)(C, B)/IN625 composite coating was found to be lower than that of the IN625 coating, and the average wear weight loss was only 10% of that of the IN625 coating, attributable to the in-situ authigenic TiCB, TiC, NbMo3B4 and NbMo2B2 phases providing load transfer from the hard phases to the IN625 composite matrix to achieve abrasion reduction and wear resistance. It was also found that the formation of nano-equiaxial ultrafine grains in the depth range of 250 nm below the wear surface was facilitated by the coupling of the three fields of plastic rheology-heat-force, which dynamically strengthened the wear surface. Based on these findings, it is suggested to promote the strategy of combing USLC and DRS techniques to achieve an additional ability to enhance the coating microstructure and reduce residual stress, to achieve better tribological performance.

Effect of surface morphology and microstructure on the hot corrosion behavior of TiC/IN625 coatings prepared by extreme high-speed laser cladding

Microstructural evolution and high-temperature oxidation of TiC/IN625 coatings fabricated by multi-layer extreme high-speed laser cladding

Effect of oxide film on corrosion behavior of NiTi coating prepared by extreme high-speed laser cladding

Microstructure, Tribocorrosion and Corrosion Performances of Laser Cladded Ni625-xTiC Coatings in 3.5% NaCl Solution

Effect of TiC addition on the microstructure and properties of laser cladding Ni60A coatings on H13 steel surface

Improved Microstructure and Wear Resistance of (cocrni)82al9ti9 Cladding Layers Via Extreme High-Speed Laser Cladding

Effect of Heat Treatment on Microstructure and Tribocorrosion Performance of Laser Cladding Ni-65 WC Coating

Effect of Ti Content on the Microstructure and Corrosion Resistance of CoCrFeNiTix High Entropy Alloys Prepared by Laser Cladding

Microstructure, Hardness and High-Temperature Corrosion Behaviors in Sulfur-Containing Environment of Laser Cladding Y2O3/IN625 Composite Coating

Effect of Co/TiAl on Mechanical Properties of Laser Melted IN 625 on 304SS Matrix

Study on fabrication of multi-phase reinforcement coatings on Ti6Al4V by laser cladding for enhanced tribological performance

Characterization of the Structure, Mechanical Properties and Erosive Resistance of the Laser Cladded Inconel 625-Based Coatings Reinforced by TiC Particles

Microstructures and Properties of Laser Cladding Al-TiC-CeO₂ Composite Coatings

Microstructure, thermostability and tribological behavior of composite CoCrFeNiTix high-entropy alloy coatings fabricated by laser cladding

Microstructure and Properties of CoCrFeNiMnTix High-Entropy Alloy Coated by Laser Cladding

Microstructure and Mechanical Properties of TiC/WC-Reinforced AlCoCrFeNi High-Entropy Alloys Prepared by Laser Cladding

Microstructure and properties of Ti–Al–C composite coatings prepared by laser cladding

(Ti, Nb)(C, B)/IN625 In-Situ Reactive Coating Prepared by Ultra-High-Speed Laser Cladding: Interfacial Characterization, Residual Stress and Surface Wear Mechanisms

Effects of TiC on the Microstructure, Mechanical Properties, and Wear Behavior of E690 Steel Prepared by Laser Cladding

Microstructure regulation and performance of titanium alloy coating with Ni interlayer on the surface of mild steel by laser cladding

Investigation into corrosion and wear behaviors of laser-clad coatings on Ti6Al4V