Abstract:The purposes of this study are to reduce Fe2O3 using hydrogen (H2) and carbon monoxide (CO) gases at a high temperature zone (500 °C–900 °C) by focusing on the influence of reduction gas concentrations. Reduction behavior of hematite (Fe2O3) at high temperature was examined using temperature programmed reduction (TPR) under non-isothermal conditions with the presence of 10% H2/N2, 20% H2/N2, 10% CO/N2, 20% CO/N2 and 40% CO/N2. The TPRCO results indicated that the first and second reduction peaks of Fe2O3 at a temperature below 660 °C appeared rapidly when compared to TPRH2. However, TPRH2 exhibited a better reduction in which Fe2O3 entirely reduced to Fe at temperature 800 °C (20% H2) without any remaining of wustite (FeO) whereas a temperature above 900 °C is needed for a complete reduction in 10% H2/N2, 10% and 20% CO/N2. Furthermore, the reduction of hematite could be improved when increasing CO and H2 concentrations since reduction profiles were shifted to a lower temperature. Thermodynamic calculation has shown that enthalpy change of reaction (ΔHr) for all phases transformation in CO atmosphere is significantly lower than in H2. This disclosed that CO is the best reductant as it is a more exothermic, more spontaneous reaction and able to initiate the reduction at a much lower temperature than H2 atmosphere. Nevertheless, the reduction of hematite using CO completed at a temperature slightly higher compared to H2. It is due to the presence of an additional carburization reaction which is a phase transformation of wustite to iron carbide (FeO → Fe3C). Carburization started at the end of the second stage reduction at 600 °C and 630 °C under 20% and 40% CO, respectively. Therefore, reduction by CO encouraged the formation of carbide, slower the reduction and completed at high temperature. XRD analysis disclosed the formation of austenite during the final stage of a reduction under further exposure with high CO concentration. Overall, less energy consumption needed during the first and second stages of reduction by CO, the formation of iron carbide and austenite were enhanced with the presence of higher CO concentration. Meanwhile, H2 has stimulated the formation of pure metallic iron (Fe), completed the reduction faster, considered as the strongest reducing agent than CO and these are effective at a higher temperature. Proposed iron phase transformation under different reducing agent concentrations are as followed: (a) 10% H2, 20% H2 and 10% C; Fe2O3 → Fe3O4 → FeO → Fe, (b) 20% CO; Fe2O3 → Fe3O4 → FeO → Fe3C → Fe and (c) 40% CO; Fe2O3 → Fe3O4 → FeO → Fe3C → Fe → F,C (austenite).

Reaction kinetics of direct reduction of mineral iron carbonate with hydrogen; determination of the kinetic triplet

Kinetic Mechanism Development for the Direct Reduction of Single Hematite Pellets in H2/CO Atmospheres

A Laboratory Study of the Reduction of Iron Oxides by Hydrogen

Kinetic Analysis of Isothermal and Non-Isothermal Reduction of Iron Ore Fines in Hydrogen Atmosphere

Kinetic analysis of iron ore powder reaction with hydrogen—carbon monoxide

Kinetics and microstructural changes during fluidized reduction of magnetite with hydrogen at low temperatures

Studies on the Reduction Behavior of Iron Oxide Pellet Fines with Hydrogen Gas: Mechanism and Kinetic Analysis

Correlating Chemical Reaction and Mass Transport in Hydrogen-based Direct Reduction of Iron Oxide

Reduction kinetics of iron oxide pellets with H2 and CO mixtures

Effect of pressure on direct reduction of mineral iron carbonate with hydrogen

Influence of hydrogen and carbon monoxide on reduction behavior of iron oxide at high temperature: Effect on reduction gas concentrations

Reduction kinetics of iron ore concentrate particles relevant to a novel green ironmaking process

Kinetics analysis of direct reduction of iron ore by hydrogen in fluidized bed based on response surface methodology

Following the Structural Changes of Iron Oxides during Reduction under Transient Conditions

The Reduction Mechanism and Kinetics of Fe2O3 by Hydrogen for Chemical-Looping Hydrogen Generation

On the Kinetic Mechanisms of the Reduction and Oxidation Reactions of Iron Oxide/Iron Pellets for a Hydrogen Storage Process

Study on the reduction of Fe2O3 pellets by CO-CO2 and H2-H2O: Reaction kinetics and pore network model

Stepwise Reduction Kinetics of Iron-Based Oxygen Carriers by CO/CO 2 Mixture Gases for Chemical Looping Hydrogen Generation

Clean iron production through direct reduction of mineral iron carbonate with low-grade hydrogen sources; the effect of reduction feed gas composition on product and exit gas composition

Kinetic Analysis of the Iron Oxide Reduction Using Hydrogen-Carbon Monoxide Mixtures as Reducing Agent

Hydrogen-based direct reduction of combusted iron powder: deep pre-oxidation, reduction kinetics and microstructural analysis