Corrosion Behavior and Microstructure of 2024 Aluminum Alloy Sheets by Shot Peen Forming in a Salt Spray Environment

DOI: https://doi.org/10.1007/s11665-022-07389-w

IF: 2.3

2022-09-29

Journal of Materials Engineering and Performance

Abstract:Shot peen forming is an important method for preparing aircraft wall panels, but it introduces residual compressive stress fields on a material′s surface, as well as surface roughness and defects. The corrosion behavior of a shot peen-formed aluminum alloy sheet (FPA) in a salt spray environment was studied. The results demonstrated that the corrosion rates of FPA samples were faster than those without shot peen forming, especially during the initial stage. Both FPA-treated and untreated samples experienced pitting, but the pits in the FPA-treated sample were larger and deeper. The cross-sectional analysis of the corrosion layer showed that the corrosion layer of the shot-peened sheet was thicker, and the anodic oxidation protective film was easily broken. Intergranular corrosion of the FPA-treated sample occurred in a salt spray environment after only 10 min, and the corrosion pits were 35.04 μm deep. For samples without FPA treatment, intergranular corrosion occurred after 5 h of salt spray corrosion. The cracks that formed after shot peen forming acted as corrosion channels that increased the corrosion susceptibility of the aluminum alloy. After shot peen forming, the impedance value and the radius of capacitive resistance arc of the samples decreased in the process of salt spray corrosion, indicating that the corrosion resistance of the alloys was reduced.

materials science, multidisciplinary