High-Temperature Corrosion Resistance of Ti-555 Titanium Alloy after Equal Channel Angular Pressing and Heat Treatment

Xu, Xiaojing

DOI: https://doi.org/10.1007/s11665-022-07440-w

IF: 2.3

2022-10-04

Journal of Materials Engineering and Performance

Abstract:This paper used Ti-5.4Al-4.1Mo-5 V-3Cr-1Zr (Ti-555) as the study material, and secondary processing methods consisting of the combination of equal channel angular pressing (ECAP) and heat treatment were adopted. The effect of different processes such as 820/880 °C solid solution-580 °C aging, 820 / 880 °C solid solution-ECAP-580 °C aging, and ECAP-820/880 °C solid solution-580 °C aging on the high-temperature corrosion behavior of the alloy was studied in 75 wt.% NaCl + 25 wt.% Na 2 SO 4 at 800 °C for 40 h. The corrosion characteristics of the alloy were evaluated via scanning electron microscope (SEM), optical microscope (OM), and x-ray diffraction (XRD). The result shows that the weight gain curve tends to be stable after 35 h, and the lowest weight gain was observed in the alloy treated at 880 °C solid solution-ECAP-580 °C, which is 0.88 mg·cm −2 . The corroded surface is mainly composed of TiO 2 and Al 2 O 3 . The thickness of the corroded section of the titanium alloy aged at 820/880 °C solid solution-ECAP-580 °C is 70 and 50 μm, respectively. Overall, the best high-temperature corrosion resistance of the Ti-555 alloy was obtained when subjected to 880 °C solid solution-ECAP-580 °C aging treatment.

materials science, multidisciplinary