Abstract:Laser ultrasound is a widely used tool for industrial quality assurance when a contactless and fast method is required. In this work, we used a laboratory setup based on a confocal Fabry–Perot interferometer to examine weld seam models. The focus was placed on small samples with curved surfaces (small in the sense that the radius of curvature is comparable to the largest ultrasonic wavelength) and on efficient ways to detect the presence and volume of process pores, with the goal to transfer this method to industrial applications. In addition to this experimental method for investigating welds, a numerical method that models the experimental setup was implemented in MATLAB. For this purpose, first the thermal effects of the excitation process were taken into account by solving the thermal diffusion equation with an explicit scheme. Then, the elastodynamic equations were solved using the Elastodynamic Finite Integration Technique, taking into account the stresses induced by the excitation process. The B-Scans generated with this numerical model were compared with experimental B-Scans for simple test cases and good agreement was found. In a next step, the additional structures in the B-Scans resulting from air inclusions were identified and investigated with both methods using flat test specimens at first. Besides the direct echoes, structures from skimming surface waves and multiple reflections were visible. These additional structures are unwanted in defect reconstruction methods like the Synthetic Aperture Focusing Technique (SAFT) as they would lead to artifacts. In samples much larger than the largest ultrasound wavelength, however, these unwanted structures are still negligible in amplitude or can be well separated temporally, but for small samples this is no longer the case. As a result, reconstruction methods based on direct echoes like SAFT are difficult to apply. For many industrial applications, the reconstruction is not decisive at all, but only the knowledge of the total volume of process pores (TVPP). It is shown with both experimental and numerical methods, that this TVPP can be estimated from the variation in the B-Scans from various small weld seam models.

Ultrasonic Testing of Welds in Thin-Walled Titanium Shells Using an Incomplete Penetration Indicator

Ultrasonic Guided Wave-Based Circumferential Scanning of Plates Using a Synthetic Aperture Focusing Technique

Ultrasonic Technique For Testing Cold Welding Of Butt-Fusion Joints In Polyethylene Pipe

Non-destructive Testing of Quality of Welded Joints of Titanium Plates of Superminiature Eddy-Current Probes

Weld Quality Inspection of Small-Diameter Thin-Walled Pipes by a Laser Ultrasonic Method.

A Review of Ultrasonic Testing Applications in Spot Welding: Defect Evaluation in Experimental and Simulation Results

Evaluation of Welded Lap Joints Using Ultrasonic Guided Waves

Evaluating Technology of Spot Weld Quality for Coated High Strength Steel Sheet Based on Ultrasonic Guide Wave

Efficient testing of weld seam models with radii of curvature in the millimeter range using laser ultrasound

Ultrasonic signal simulation for thick-walled welds based on ray-tracing algorithm and ultrasonic field calculation

Analysis of the Suitability of Ultrasonic Testing for Verification of Nonuniform Welded Joints of Austenitic–Ferritic Sheets

Ultrasonic and phased-array inspection in titanium-based alloys: A review

Ultrasonic testing of thick and thin Inconel 625 alloys manufactured by laser powder bed fusion

Ultrasonic Testing of Welded Joints in Polyethylene Pipe

Ultrasonic and structural characterization of anisotropic austenitic stainless steel welds: Towards a higher reliability in ultrasonic non-destructive testing

Application of advanced ultrasonic testing methods to Dissimilar Metal Welds -- Comparison of simulated and experimental results

Design and Application of Partial Immersion Focused Ultrasonic Transducers for Austenitic Weld Inspection

Estimation of the Size and Location of an Artificial Weld Seam Defect Based on the Actual Ultrasonic Welding Phenomenon for Online Inspection

SIMULATION OF DEFECTS IN ULTRASONIC TESTING OF WELDED JOINTS

Imaging of Ultrasonic SH Wave Inspection of Thick-walled Welds Based on Array Technology

Early detection of steel tube welded joint failure using SPC-I nonlinear ultrasonic technique