Abstract:The most of commercial isotactic polypropylene (PP) polymers exhibit low melt strength due to lack of a long-chain-branched (LCB) structure, which significantly limits PP processing operations. There are several chemical methods available today to prepare high-melt-strength PP (HMS-PP) products containing a small amount of LCB structures. However, the processes require multiple reaction steps, forming a complicated mixture of branch structures (i.e., branch length, branch density, and impurity, etc.). This work discusses an efficient and economic method following a commercial PP production process (i.e., polymerization and then extrusion). The direct-polymerization step is centered on an asymmetric diene co-monomer p-(3-butenyl)styrene (BSt) that can be randomly incorporated in the PP chain with a mono-enchainment fashion by the fourth generation MgCl2-supported TiCl4 catalyst in the slurry polymerization process. The predominate coordination/1,2-insertion of the α-olefin moiety in the BSt co-monomer forms linear PP-co-BSt copolymer (granules), with few pendant styrene moieties randomly distributed along the polymer chain. Following the common PP extruding and pelletizing procedure at 200 °C, the molten PP-co-BSt copolymer engages the in situ coupling reaction between pendant styrene units in neighboring polymer chains to spontaneously form PP branches with long branch lengths. The branch densities in the resulting LCB-PP pellets are controlled by the BSt content in the copolymer and the degree of the thermally induced coupling reaction. The resulting LCB-PP polymer, with an average of one to four LCB structures per chain, is completely melt-processable, exhibiting high melt strength under elongation flows. The same strain-hardening phenomenon was also observed in the polymer blends between these LCB-PP polymers and linear PP homopolymer with the composition up to 1/1 weight ratio.

Polymerization in the Borstar Polypropylene Hybrid Process: Combining Technology and Catalyst for Optimized Product Performance

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

Blending Properties of Polyethylene Blends Obtained by Hybrid Catalyst on Composite Support

Experimental Investigation on Mechanisms of Fine Particles Generation for the Borealis Borstar Multistage Olefin Polymerization Process

Control of Diffusion/Barrier Effects of Polymer-Coated Particles and the Strengthening of Ethylene Polymerization Reactor

Integrated Ziegler‐Natta/Brookhart‐Ni Catalysts for the Synthesis of Sutured Polar High‐Impact Polypropylenes

β-Modification in heterogeneous polypropylene for laser-based powder bed fusion of polymers

Process Intensification Of Polymerization Processes With Embedded Molecular Weight Distributions Models: An Advanced Optimization Approach

Preparation of Well-Controlled Isotactic Polypropylene-Based Block Copolymers with Superior Physical Performance via Efficient Coordinative Chain Transfer Polymerization

Recent Advances in Nickel Catalysts with Industrial Exploitability for Copolymerization of Ethylene with Polar Monomers

Direct Synthesis of High-Melt-Strength Polypropylene Using the Fourth Generation Heterogeneous Ziegler–Natta Catalyst and Commercial Production Process

Versatile Polypropylene Copolymers from a Pilot-Scale Spheripol II Process

Ethylene Polymerization with Hybrid Nickel Diimine/cp2ticl2 Catalyst: a New Method to Prepare Blends of Linear and Branched Polyethylene

Influence of Copolymerization Conditions on the Structure and Properties of Polyethylene/Polypropylene/Poly(Ethylene-Co-Propylene) In-Reactor Alloys Synthesized in Gas-Phase with Spherical Ziegler-Natta Catalyst

An Atmosphere-Switching Polymerization Process: A Novel Strategy To Advanced Polyolefin Materials

Bimodal polyethylene – Interplay of catalyst and process

Accelerating the Research Approach to Ziegler–Natta Catalysts

Solid Phase Graft Polymerization of Styrene in Spherical Polypropylene Granules

Synthesis of Polypropylene/poly(ethylene-co-propylene) In-Reactor Alloys by Periodic Switching Polymerization Process: Dynamic Change of Gas-Phase Monomer Composition and Its Influences on Polymer Structure and Properties

Progress in synthesis methods of polypropylene-based block copolymers

Vulcanization of polypropylene