Abstract:Schematic representation of the proposed process in trimodal polymerization. Trimodal polymerization of polyethylene has become a research interest in recent years due to its excellent potential for altering material properties and overcoming the limitations of the bimodal process. Here, we have comprehensively investigated the effects of manipulating polymerization parameters, such as split value (SV), hydrogen‐to‐ethylene ratio (H2/C2), and stage switching, on the rheological, thermal, and mechanical properties of synthesized trimodal high‐density polyethylene (HDPE). The synthesized samples were obtained through three consecutive stages in a slurry lab‐scale reactor. The results of molten state analysis demonstrate that recipe modification, particularly SV and H2/C2 balancing in the second and third stages, had a dramatic effect on the rheological properties including dynamic moduli, G′‐G′′ crossover, and the shear‐thinning behavior. Concurrently, improvements in physio‐mechanical properties, such as sagging behavior and slow crack growth resistance (SCG), were observed compared to the bimodal resin. The thermal characterization indicates that the polymerization adjustments made did not notably impact the thermal properties of HDPE samples (e.g., Tm), throughout the all‐recipe manipulation. However, minor fluctuations in crystallinity and crystallization kinetics were observed which was presumably attributed to the molecular weight of the final resin. Overall, in our trimodal polymerization recipe, the HDPE powder is within the specified range of particle size distribution, which ensures excellent bulk density and flowability. Highlights Influence of polymerization parameters such as split value, H2/C2, and stage switching in properties of trimodal HDPE. HDPE resin received from split value and H2/C2 balancing have superior SCG and sagging resistance. All HDPE samples synthesized by different recipes have similar thermal properties.

Bimodal polyethylene – Interplay of catalyst and process

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

Blending Properties of Polyethylene Blends Obtained by Hybrid Catalyst on Composite Support

Simulation of Bimodal Polyethylene Production by Oscillating Operation of Hydrogen

Control of Diffusion/Barrier Effects of Polymer-Coated Particles and the Strengthening of Ethylene Polymerization Reactor

Preparation of Polyethylene Elastomers with Increased High Molecular Weight and Nearly Perfect Strain Recovery by Steric Control of Asymmetric Α-Diimine Nickel Catalyst

Synthesis of Polyethylene with Bimodal Molecular Weight Distribution by Supported Iron‐based Catalyst

Influence of trimodal polymerization on melt rheology, thermal, and mechanical properties of HDPE resin

Synthesis of Bimodal Polyethylene Using Ziegler-Natta Catalysts by Multiple H2 Concentration Switching in a Single Slurry Reactor

Exploring bimodal HDPE synthesis using single- and dual-site metallocene catalysts: a comprehensive review of the Monte Carlo method and AI-based approaches

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

Facile Preparation of Bimodal Polyethylene with Tunable Molecular Weight Distribution from Ethylene Polymerization Catalyzed by Binary Catalytic System in the Presence of Diethyl Zinc

Dual Bimodal Polyethylene Prepared By Intercalated Silicate With Nickle Diimine Complex

Polyethylene Materials with In-Chain Ketones from Catalytic Copolymerization

One Pot Synthesis of Bimodal Uhmwpe/Hdpe In-Reactor Blends with Cr/V Bimetallic Catalysts

Research progress of bimetallic catalysts for bimodal polyethylene synthesis

A comparative Monte Carlo simulation of HDPE synthesis with bimodal molecular weight distribution: evaluating slurry and solution processes using dual-site metallocene catalyst

Evaluation and Control of the Molar Mass Bimodality and Properties of Polyethylene from Novel Chromocene-Based Dual Sites Catalysts

A co-anchoring strategy for the synthesis of polar bimodal polyethylene

Ethylene Polymerization with Hybrid Nickel Diimine/cp2ticl2 Catalyst: a New Method to Prepare Blends of Linear and Branched Polyethylene

Novel SiO2‐Supported Chromocene and Vanadium Bimetallic Catalysts Producing Bimodal Polyethylene