Abstract:Electrical explosion, characterized by ultrafast heating (dT/dt ∼ 1011 K/s) and quenching (1010 K/s) rates of the sample, is a powerful tool for synthesizing graphene-related materials. Experiments were performed with graphite plate in water and Cu wire in graphite-powder-contained tube, to determine the influence of the confined environment on the morphology of the products. As a comparison, an Al-coated carbon foil was exploded in free air. High-speed photography along with electrophysical and optical diagnostics were applied to characterize the electrical explosion. Accordingly, SEM, EDS, and XPS were used to characterize the explosion products. The results reveal that the confined environment prevents the discharge channel from expanding or limiting at a certain diameter so that the products quench in a confined environment that is different from free air. In water and tube explosions, due to the shockwave and the expansion of the discharge channel, the graphite products are compacted to the baseplate, namely, the interface of the water medium and tube wall, respectively. Stacked graphite sheets are formed as a result. Based on the high-speed photography and SEM results, the synthesized graphite is partly exfoliated in the confined environments; consequently, thin graphite nanosheet (less than 10 nm) is observed in the marginal areas. The mechanism of exfoliation is preliminarily analysed in water and tube explosion. Furthermore, a composite material is obtained in tube explosion, and the structure is stacked graphite sheets with spherical copper nanopowder adhering to it. As a comparison, when exploding in free air, typical spherical nanoparticles are synthesized for both elements; finally, the discrepant formation mechanisms of products in confined or unconfined environments are simply discussed.

Deagglomeration of polycrystalline diamond synthesized from graphite by shock-compression

Synthesis of Nano-Polycrystalline Diamond under High Pressure and High Temperature

Synthesizing bulk polycrystalline diamond by method of direct phase transition

Nano-polycrystalline diamond formation under ultra-high pressure

Diamond Micropowder Synthesis Via Graphite Etching in a Microwave Hydrogen Plasma

Study on the Polycrystalline Mechanism of Polycrystalline Diamond Synthesized from Graphite by Direct Detonation Method

Nano-Graphite Synthesized by Explosive Detonation and Its Application in Preparing Diamond under High-Pressure and High-Temperature

The growth of agglomerates in the conditions of detonation synthesis of diamond

Diamond synthesized by using natural flake graphite without sulfur

Extrastrong aggregates of detonation nanodiamonds: structure and formation

A simple and soft chemical deaggregation method producing single-digit detonation nanodiamonds

Structure formation of ultradispersed diamond by detonation synthesis

Synthesis of diamond using nano-graphite and Fe powder under high pressure and high temperature

Diamond Films and Particles Growth in Hydrogen Microwave Plasma with Graphite Solid Precursor: Optical Emission Spectroscopy Study

Fabrication process independent and robust aggregation of detonation nanodiamonds in aqueous media

Shear-promoted Graphite-to-diamond Phase Transition at the Grain Boundary of Nanocrystalline Graphite

Study on purification and properties of ultrafine diamond prepared by explosive technique

Large Area Single-Crystal Diamond Synthesis by 915 MHz Microwave Plasma-Assisted Chemical Vapor Deposition

Scalable Reshaping of Diamond Particles via Programmable Nanosculpting

Size tunable synthesis of solution processable diamond nanocrystals.

One-step preparation of pure and Cu-decorated graphite thin layers via electrical explosion in a confined environment: Physical process and product characterization