Abstract:In this study, the effect of colloidal nano-silica replacing a fraction of cement and recycled concrete fine aggregate replacing natural sand on the post-fire mechanical features and durability of concrete was explored. To achieve this goal, 189 concrete samples were manufactured in total, with key variables being the volume of fine aggregate at 0, 50, and 100% replacing natural fine aggregate, the volume of nano-silica at 1.5, 3, 4.5, and 6% replacing the cement weight, and the exposure temperature at 20, 300, and 600 °C. Parameters selected for consideration in the concretes consisted of compressive capacity, splitting tensile capacity, elastic modulus, ultrasonic pulse velocity (UPV), and weight loss. Furthermore, using scanning electron microscopy (SEM) imaging, the microstructural condition of different sample groups was investigated. According to the findings, as the content of the recycled fine aggregate (RFA) replacing natural fine aggregate increased, the compressive capacity of the unheated and heated concretes declined, and the rate of this drop became greater as the replacement volume increased. On the other hand, the presence of the nano-silica and an increase in its content replacing the cement content in recycled aggregate concrete improved the compressive strength relative to the reference concrete for all the exposure temperatures, with the greatest improvement for the replacement percentage of 4.5%. In addition, the heat-induced compressive capacity drop was more pronounced at higher replacement levels of nano-silica. With a rise in the exposure temperature of the samples with only the recycled fine aggregate, fewer microcracks formed compared with the samples containing both recycled fine aggregate and nano-silica. The maximum weight loss occurred in the recycled sample containing the highest contents of nano-silica and recycled aggregate. Afterward, it was attempted to estimate the mechanical features of concrete by developing several empirical formulas as a function of temperature and volume fractions of recycled fine aggregate and nano-silica. These formulas were evaluated against the test data of this study and others, which showed an acceptable correlation. Finally, the findings of the tests were evaluated against the predictions of ACI 216, EN 1994–1-2, EN 1992–1-2, and ASCE.

The Effect of Homogenization Procedure on Mechanical Properties of High-Performance Concrete with Partial Replacement of Cement by Supplementary Cementitious Materials

Effect of four-component binder on characteristics of self-compacting and fibre-reinforced self-compacting mortars

Study on performance of high strength pumping concrete compounded by fly ash composite powder under low water-cement ratio

Pre- and post-heating mechanical properties of concrete containing recycled fine aggregate as partial replacement of natural sand and nano-silica as partial replacement of cement: experiments and predictions

Effect of Dolomite and Metakaolin on the Properties of High-Performance Concrete

Identification of multi-scale homogeneity of blended cement concrete: macro performance, micro and meso structure

Mechanical and Durability Properties of High Strength Concrete Incorporating Different Combinations of Supplementary Cementitious Materials: A Review

Mechanical Properties and Durability of High-Performance Concretes Blended with Circulating Fluidized Bed Combustion Ash and Slag as Replacement for Ordinary Portland Cement

Mechanical properties and microstructure of ultra-high performance concrete with low cement content

Effects of the sole or combined use of chemical admixtures on properties of self-compacting concrete

Mechanical Properties and Chloride Penetration Resistance of Concrete Combined with Ground Granulate Blast Furnace Slag and Macro Synthetic Fiber

Mechanical properties and micro-structure analysis of concrete adding high performance composite cementious material

THE MECHANICAL STRENGTH AND DRYING SHRINKAGE BEHAVIOR OF HIGH PERFORMANCE CONCRETE WITH BLENDED MINERAL ADMIXTURE

Influence of Mixture Proportions on Fresh and Mechanical Properties of Self-consolidating Concrete

Concrete Mix Strength and Permeability with Various Supplementary Cementitious Materials

Influence of alkali metal formates and calcium formate on workability, hydration and basic properties of reactive powder concrete

Experimental Investigation and Image Processing to Predict the Properties of Concrete with the Addition of Nano Silica and Rice Husk Ash

The Influence of Superabsorbent Polymers and Nanosilica on the Hydration Process and Microstructure of Cementitious Mixtures

Analyzing the Mechanical, Durability, and Microstructural Impact of Partial Cement Replacement with Pumice Powder and Bamboo Leaf Ash in Concrete

Influence of nanoparticles in UHPC by intensive (vacuum) mixing studies

INVESTIGATING THE EFFECT OF NANO SILICA ON THE MECHANICAL PROPERTIES OF HARDENED CEMENT PASTE