Abstract:This study explores an efficient and feasible method for production of non-commercial Co-Cr-Mo powder feedstock for Laser Powder Bed Fusion (LPBF), employing mechanical alloying (MA) with following thermal treatment. Elemental Co, Cr, and Mo powders were subjected to MA to create a powder nanostructured composite. Initially, the mechanically alloyed powder had a mixed-phase state, with ε-phase as the main one (about 95 wt%) and impurities of Cr 2 O 3 . However, an additional 1.5-hour of isothermal annealing at 400 °C successfully reduced the Cr 2 O 3 impurities and caused oxygen content to decrease, indicating a reduction in residual oxygen in the powder. This annealing process activated diffusion and induced relaxation of residual stresses, evidenced by decreased lattice microstrains: 0.8% for the Co-phase, 0.2% for both the Cr-phase and Mo-phase. Powder subjected to the thermal treatment was then utilized in LPBF to create bulk Co-Cr-Mo samples. The formed samples showed a typical LPBF microstructure represented by uniaxial cells and dendrites, with the distance between these structures not exceeding 3 μm. The samples showed homogenous elemental distribution, mixed-phase composition, and oxygen concentration not exceeding 5 wt%. In terms of mechanical properties , the LPBF samples exhibited a microhardness value of 4300 ± 200 MPa, ductility of 0.85, and yield strength of 1.4·10 3 MPa. Our method yields results comparable to those obtained from commercially spherical powder, indicating that our cost-effective approach does not sacrifice product quality. It represents a substantial cost reduction, approximately 4.5 times lower than that of commercial spherical powder, thereby highlighting the economic efficiency of our powder feedstock preparation for LPBF. Our findings underscore the potential of mechanically alloyed and thermally treated powder in LPBF. This worthwhile and efficient method of preparation powder feedstock breaks ground for more comprehensive facilities in 3D printing, cut down on cost of production with maintaining the high-quality output.

Synthesis of Tree-Component Cobalt-Based Alloy by Selective Laser Melting

Structure and properties of a cobalt-chromium-molybdenum alloy obtained by selective laser melting

X-ray spectral microanalysis of hardened additive products made of electroerosion cobalt-chromium alloys

Tailoring the tribology property and corrosion resistance of selective laser melted CoCrMo alloys by varying copper content

In Situ Reactive Formation of Mixed Oxides in Additively Manufactured Cobalt Alloy

From Raw Elements to 3D Samples: An Economical Route for Co-Cr-Mo Alloy Fabrication

Microstructures Of Components Synthesized Via Electron Beam Selective Melting Using Blended Pre-Alloyed Powders Of Ti6al4v And Ti45al7nb

Additive Manufacturing of Cobalt-Based Dental Alloys: Analysis of Microstructure and Physicomechanical Properties

Effect of the Addition of Cu and Al on the Microstructure, Phase Composition and Properties of a Ti-6Al-4V Alloy Obtained by Selective Laser Melting

First attempt to print Co-based alloys with high glass forming ability by selective laser melting

INVESTIGATING THE POSSIBILITY OF ALLOYING AN ALLOY ALSI25CU5CR WITH CO, CR AND MO USING METAL POWDER

Structure and Properties of Cobalt-Based Superalloys After Electron Beam Additive Manufacturing

The Effects of Co on the Microstructure and Mechanical Properties of Ni-Based Superalloys Prepared via Selective Laser Melting

Mechanical Behavior of a Medium-Entropy Fe65(CoNi)25Cr9.5C0.5 Alloy Produced by Selective Laser Melting

Selective Laser Melting of Multi-Principal NiCrWFeTi Alloy: Processing, Microstructure and Performance

Characteristics of Biometallic Alloy to Additive Manufacturing Using Selective Laser Melting Technology

Microstructure Evolution of FeNiCoCrAl1.3Mo0.5 High Entropy Alloy during Powder Preparation, Laser Powder Bed Fusion, and Microplasma Spraying

Effects of Co on the Microstructure Evolution and Mechanical Properties of Ti-4Al-6Cr-5Mo-8Nb Alloy by Ultrasonic Vacuum Melting

Strengthening Mechanisms of Combined Alloying with Carbon and Titanium on Laser Beam Welded Joints of Molybdenum Alloy

Intermetallic compound formation during laser alloying of aluminum alloys with metals

In-Situ Alloy Formation of a WMoTaNbV Refractory Metal High Entropy Alloy by Laser Powder Bed Fusion (PBF-LB/M)