Abstract:Good gas permeability is an essential factor for the smooth operation and high performance in the lower part of the blast furnace. Under the present low carbon blast furnace smelting conditions, the coke layer is thinner, and the proportion of the molten metal in the coke layer is significantly higher, resulting in a major reduction in gas permeability, which seriously affects blast furnace operations. Also, the lower thickness of the coke layer weakens the process of solid-liquid carbon dissolution when the molten iron passes through the coke layer, which reduces the carbon content of the molten iron and further deepens the erosion of the refractory by the unsaturated molten iron. The carbon dissolution in the molten iron in a blast furnace core was measured by a high-temperature vacuum wettability test tool that analyzed the interface wetting activity between Fe−C melts with specific carbon mass fraction (3.8%, 4.3%, 4.8%) and 99.9% of high temperatures graphite plates. Besides, the scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the graphite substrate’s carburizing morphology and carburizing distances. The results show that, with the increase of carbon content, the interface contact angle becomes bigger. The contact angle decreases with time, and eventually reaches a steady-state during the melting process, and the Fe−C melt with saturated carbon cannot be wet. The scanning electron microscopy analysis shows that a spherical cap-like depression is created by a cross-section of the Fe−C melt and the graphite substrate, and the radius and volume of the depression decrease with increasing carbon content. The study of the EDS scanning analysis shows that the amount of dissolved carbon atoms in the graphite substrate penetrates the Fe−C melt and decreases with increasing initial carbon concentration. The smaller the carburizing effect, the better the wetting is conducive to carbon mass transfer. It is found that by measuring carburizing of the carbon atoms in the graphite substrate into the Fe−C melt by calculating the surface energy reduces the surface energy between the two. Thus, the surface tension decreases and the melt spreads slowly with contact angle gradually decreasing during melting.

Influence of Coke Deterioration Behavior in Blast Furnace on Microcrystalline Structure Characteristics

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

Pore Structure Evolution During the Coke Graphitization Process in a Blast Furnace

Microstructure and Melting Loss Behavior of Blast Furnace Incoming Coke and Radial Tuyere Coke

A study on the characteristics of coke in the hearth of a superlarge blast furnace

Microstructure Analysis and Mineral Phase Transformation of Coke in Blast Furnace

Microstructure Evolution Behavior of Blast-Furnace Coke under Different Gasification Reaction Conditions

Effect of gasification reaction on pore structure, microstructure, and macroscopic properties of blast furnace coke

Effect of blast furnace coke graphitizing its high temperature metallurgical properties

Existence State and Structures of Extracted Coke and Accompanied Samples from Tuyere Zone of a Large-Scale Blast Furnace

“In situ” studies on cokes drilled from tuyere to deadman in a large-scale working blast furnace

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Effect of high temperature on macroscopic properties and microstructure of metallurgical coke

Behavior of coke in the blast furnace for smelting Bayan Obo Mine

Degradation Behaviors of Coke under Complex Solution Loss Conditions

Study on Deterioration Behavior of Coke During Gasification

Strength degradation mechanism of iron coke prepared by mixed coal and Fe2O3

A comprehensive investigation on the structural transformation and dissolution loss reaction of coke during gasification in CO 2 atmosphere

Influence of Sodium on Coke Microstructure in Different Reaction Atmosphere

Influence of Structure and Mineral Association of Tuyere-Level Coke on Gasification Process

Physical and chemical properties of metallurgical coke and its evolution in the blast furnace ironmaking process