Abstract:Herein, ordinary silicate concrete specimens are prepared to study the damage law of a cement-concrete material under the effects of salt erosion and a freeze–thaw environment. NaCl, NaHCO3, and Na2SO4 solutions are separately produced, according to the characteristics of saline soil, to conduct an experimental study on the concrete characteristics during quick salt freezing cycles, and to analyse the changes in its compressive strength, mass loss, and dynamic elastic modulus (DEM) under freeze–thaw cycles. Low-field nuclear magnetic resonance (NMR) and scanning electronic microscopy are used to investigate the change in the microstructure of concrete specimens under salt freeze–thaw cycles (FTCs). The results show the loss in compressive strength, mass, DEM, and NMR spectrum signal increased by 1.5–3 times, 3–5 times, 1.5–2.5 times, and 2–4 times, respectively, for concrete specimens under 50–100 FTCs in 6.8% composite salt solution, in comparison to fresh water. Apparent spalling, decreases in the DEM, and reductions in the compressive strength occur in concrete when increasing the number of salt FTCs. The number of internal cracks in the concrete structure increase under the combined action of salt crystallization, moisture absorption, and freeze–thaw. The changes in the internal microscopic pore volume in concrete structures exhibit the same trend with changes in the macro mechanical properties of concrete. The correlation coefficients between the changes in each peak in the NUR spectrum and the changes in the compressive strength of concrete specimens under FTCs in freshwater or low-concentration salt solutions are both larger than 0.7, calculated using the grey correlation degree method. Therefore, these changes could be used as a potential evaluation index for salt frozen damage to concrete structures.

Salt frost scaling of concrete – new insights regarding the damage mechanism

The peculiar behaviour of low‐carbon concretes under salt frost exposure

Salt frost attack on concrete: the combined effect of cryogenic suction and chloride binding on ice formation

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Estimation of Ice Formation in Mortar Saturated with Sodium Chloride Solutions

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Experimental Study and Mechanism Analysis on Frost Resistance of Normal Performance Concrete under Different Environments

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

A Numerical Study on Chloride Diffusion in Freeze-Thaw Affected Concrete

Frost durability of high-volume fly ash concrete: Relation liquid transport - damage

Electrical Response of Mortar Saturated with NaCl Solutions under Freeze–Thaw Cycles

Mesoscale Simulation of Bond Behaviors Between Concrete and Reinforcement under the Effect of Frost Damage with Axisymmetric Rigid Body Spring Model

Mesoscale Simulation of Concrete Behavior with Non-Uniform Frost Damage with Verification by CT Imaging

RBSM based analysis on mechanical degradation of non-air entrained concrete under frost action – A general prediction with various water cement ratio, lowest temperatures and FTC numbers

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

FROST RESISTANCE OF CONCRETE IN SALT SOLUTION

Study on the Frost Resistance of Composite Limestone Powder Concrete against Coupling Effects of Sulfate Freeze–Thaw