Abstract:In the transition towards green energy, long distance transportation of gaseous hydrogen by pipeline is considered to be an economically attractive solution. For safe transportation of hydrogen, it is important to conduct relevant mechanical tests in representative hydrogen environments and working conditions of pipelines to demonstrate acceptable hydrogen embrittlement resistance of the steel. One important issue is the testing condition for the ratio of gaseous hydrogen volume over specimen surface area required in mechanical testing since this has not been specified in any testing standards and codes or investigated. This study investigated this issue by performing slow strain rate tensile (SSRT) testing of an X52 pipeline steel in gaseous hydrogen with different ratios of hydrogen volume/specimen surface area, R v/s , ml/mm 2 . It was found that, with increasing R v/s ratio, the area reduction of the steel decreased and hydrogen embrittlement sensitivity increased in the range of the R v/s ratios investigated. The saturating R v/s ratio appeared to be ∼2.0 beyond which the effect of R v/s ratio on hydrogen embrittlement sensitivity was relatively small. The macroscopic and microscopic observations on both the fracture and side surfaces of the SSRT tested specimens also found that the tendency to cleavage fracture increased with increasing R v/s ratio. The results of the ab initio molecular dynamics (AIMD) simulations performed also predicted a dependence of hydrogen embrittlement on hydrogen volume when R v/s ratio is relatively small.

Influence of low tensile stress on the kinetics of hydrogen permeation and evolution behavior in alkaline environment

Effect of tensile stress on the hydrogen adsorption of X70 pipeline steel

Effect of Hydrostatic Pressure on Hydrogen behavior on the surface of X70 pipeline steel

Effect of tensile stress on the hydrogen permeation of MS X65 pipeline steel under sulfide films

Effects of Stress Concentration on the Mechanical Properties of X70 in High-Pressure Hydrogen-Containing Gas Mixtures

Effects of Hydrogen on the Mechanical Response of X80 Pipeline Steel Subject to High Strain Rate Tensile Tests

Investigation of hydrogen embrittlement behavior in X65 pipeline steel under different hydrogen charging conditions

Influence of hydrogen ingress on residual stress and strain in pipeline steels

The experiment study to assess the impact of hydrogen blended natural gas on the tensile properties and damage mechanism of X80 pipeline steel

Investigations of temperature effects on hydrogen diffusion and hydrogen embrittlement of X80 pipeline steel under electrochemical hydrogen charging environment

Hydrogen in Stress Corrosion Cracking of X-70 Pipeline Steels in Near-Neutral Ph Solutions

Effect of Hydrogen on Tensile Properties and Fracture Behavior of Two High-Strength American Petroleum Institute Linepipe Steels

Investigation of Hydrogen Diffusion and Trapping Behavior under Tensile Stresses in a Container Steel

Experimental study on the temperature dependence of gaseous hydrogen permeation and hydrogen embrittlement susceptibility of X52 pipeline steel

Effect of stress triaxiality on the hydrogen embrittlement micromechanisms in a pipeline steel evaluated by fractographic analysis

Effect of tempering temperature on stress-assisted hydrogen diffusion and hydrogen-induced embrittlement in a high strength low alloy steel

Influence of hydrogen volume/specimen surface area ratio on hydrogen embrittlement sensitivity of X52 pipeline steel

Study on hydrogen embrittlement susceptibility of X80 steel through in-situ gaseous hydrogen permeation and slow strain rate tensile tests

Study on the mechanical properties of X80 pipeline steel under pre-charged high-pressure gaseous hydrogen

Effect of Cold Deformation on the Hydrogen Permeation Behavior of X65 Pipeline Steel

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment