Abstract:With the rapid development of hydrogen pipelines, their safety issues have become increasingly prominent. In order to evaluate the properties of pipeline materials under a high-pressure hydrogen environment, this study investigates the hydrogen embrittlement sensitivity of X70 welded pipe in a 10 MPa high-pressure hydrogen environment, using slow strain rate testing (SSRT) and low-cycle fatigue (LCF) analysis. The microstructure, slow tensile and fatigue fracture morphology of base metal (BM) and weld metal (WM) were characterized and analyzed by means of ultra-depth microscope, scanning electron microscope (SEM), electron backscattering diffraction (EBSD), and transmission electron microscope (TEM). Results indicate that while the high-pressure hydrogen environment has minimal impact on ultimate tensile strength (UTS) for both BM and WM, it significantly decreases reduction of area (RA) and elongation (EL), with RA reduction in WM exceeding that in BM. Under the nitrogen environment, the slow tensile fracture of X70 pipeline steel BM and WM is a typical ductile fracture, while under the high-pressure hydrogen environment, the unevenness of the slow tensile fracture increased, and a large number of microcracks appeared on the fracture surface and edges, with the fracture mode changing to ductile fracture + quasi-cleavage fracture. In addition, the high-pressure hydrogen environment reduces the fatigue life of the BM and WM of X70 pipeline steel, and the fatigue life of the WM decreases more than that of the BM as well. Compared to the nitrogen environment, the fatigue fracture specimens of BM and WM in the hydrogen environment showed quasi-cleavage fracture patterns, and the fracture area in the instantaneous fracture zone (IFZ) was significantly reduced. Compared with the BM of X70 pipeline steel, although the effective grain size of the WM is smaller, WM's microstructure, with larger Martensite/austenite (M/A) constituents and MnS and Al-rich oxides, contributes to a heightened embrittlement sensitivity. In contrast, the second-phase precipitation of nanosized Nb, V, and Ti composite carbon-nitride in the BM acts as an effective irreversible hydrogen trap, which can significantly reduce the hydrogen embrittlement sensitivity.

Effects of Stress Concentration on the Mechanical Properties of X70 in High-Pressure Hydrogen-Containing Gas Mixtures

Mechanical Properties of X70 Welded Joint in High-Pressure Natural Gas/Hydrogen Mixtures

Effect of tensile stress on the hydrogen adsorption of X70 pipeline steel

Influence of Hydrogen in Natural Gas Mixed Hydrogen Environment on Mechanical Properties of X80 Pipeline Steel

Study on the mechanical properties of X80 pipeline steel under pre-charged high-pressure gaseous hydrogen

Effects of Hydrogen on the Mechanical Response of X80 Pipeline Steel Subject to High Strain Rate Tensile Tests

Hydrogen effects on X80 pipeline steel in high-pressure natural gas/hydrogen mixtures

Effect of Hydrostatic Pressure on Hydrogen behavior on the surface of X70 pipeline steel

The experiment study to assess the impact of hydrogen blended natural gas on the tensile properties and damage mechanism of X80 pipeline steel

Synergistic effect of different testing environments on the hydrogen-induced mechanical degradation to establish the role of microstructural features on the failure of X70 pipeline steel

Effect of stress triaxiality on the hydrogen embrittlement micromechanisms in a pipeline steel evaluated by fractographic analysis

Evaluating the Effect of Blended and Pure Hydrogen in X60 Pipeline Steel for Low-Pressure Transmission Using Hollow-Specimen Slow-Strain-Rate Tensile Testing

Influence of low tensile stress on the kinetics of hydrogen permeation and evolution behavior in alkaline environment

Quantitative Study on Hydrogen Concentration–Hydrogen Embrittlement Sensitivity of X80 Pipeline Steel Based on Hydrogen Permeation Kinetics

Hydrogen Embrittlement Sensitivity of X70 Welded Pipe Under a High-Pressure Pure Hydrogen Environment

The dependence of fatigue property on applied stress in X80 pipeline steel notched specimens in hydrogen gas environment

Effects of hydrogen on the fracture toughness of a X70 pipeline steel

Study on hydrogen embrittlement susceptibility of X80 steel through in-situ gaseous hydrogen permeation and slow strain rate tensile tests

Synergic Effects of Temperature and Pressure on the Hydrogen Diffusion and Dissolution Behaviour of X80 Pipeline Steel

Effects of plastic deformation on hydrogen trapping and hydrogen distribution in X80 pipeline steel

Influence of hydrogen ingress on residual stress and strain in pipeline steels