Reduction Roasting of a Titanomagnetite Concentrate with the Formation of a Titanium–Vanadium Slag Suitable for the Subsequent Recovery of Vanadium and Titanium

Goncharov, K. V.,Agamirova, A. S.

DOI: https://doi.org/10.1134/S0036029522070047

2022-08-16

Russian Metallurgy (Metally)

Abstract:The reduction roasting of the titanium–magnetite concentrate from the Gremyakha-Vyrmes deposit to produce granular cast iron and a titanium–vanadium slag has been studied. A preliminarily beneficiated titanium magnetite concentrate containing (%) 59.3 Fe tot , 7.7 TiO 2 , 1.5 SiO 2 , 0.74 V 2 O 5 , etc. is used for an investigation. The reduction roasting of the concentrate is performed with coke in the temperature range 1450–1550°C on a coal substrate. The influence of temperature, the amount of a solid reducing agent, and the addition of CaCO 3 on the formation of metal and slag phases during reduction roasting and the distribution of iron and vanadium between these phases is studied. At 3% CaCO 3 and 12–14% coke in a charge, a good separation of a slag from metallic granules is found at roasting temperatures of 1475–1500°C, and the degree of iron recovery is ~99%. According to X-ray diffraction, chemical, and microprobe analyses, the slag produced during reduction at 12% coke and 3% CaCO 3 and 1500°C contains (%) 43.6 TiO 2 , 19.8 Al 2 O 3 , 11.9 SiO 2 , 7.8 MgO, 3.35 V 2 O 5 , and so on. Its phase composition is mainly represented by anosovite and Mg–Al spinels with a small amount of glass and Ca–Mg aluminosilicate (pyroxene).