Use of orange peel extract as an inhibitor of stainless steel corrosion during acid washing in a multistage flash desalination plant

Nehal A. Barghout,Ahmed El Nemr,B. A. Abd-El-Nabey,H. A. Fetouh,Safaa Ragab,Nnabuk Okon Eddy

DOI: https://doi.org/10.1007/s10800-022-01772-0

IF: 2.925

2022-10-15

Journal of Applied Electrochemistry

Abstract:Environmentally friendly and cost-effective inhibitors based on orange peel extract (OPE) have been developed for potential applications in ejector tubes of a multistage desalination plant during the acid cleaning process. After conducting tests under both static and hydrodynamic circumstances, it was determined that the inhibitor formulation was effective against corrosion of stainless steel (SS) in 1 M HCl solution at 30 °C under the conditions tested. Electrochemical methods were used along with electron microscopy to collect information on the corrosion inhibition efficiency of the extract. Experiments were conducted for 1, 2, 3, 4, 6, 12, and 24 h, and the performance of OPE was compared to that of a commercial acid corrosion inhibitor to determine which performed better. The results revealed that OPE demonstrated outstanding corrosion inhibition performance compared to the commercial acid corrosion inhibitor. With remarkable inhibition efficacy for up to 24 h under both static and dynamic settings, 0.4% of OPE displayed typical mixed-type corrosion inhibitor behavior in the tested environment. All of the procedures that were used produced results that were in good agreement. Due to the synergistic action between the two compounds, the corrosion inhibition of OPE on SS was improved in 1 M HCl in the presence of iodide ions. In the absence of KI, OPE was found to inhibit SS corrosion at a concentration-dependent rate, with the concentration of OPE being the most significant factor. A study of the adsorption of OPE onto a SS surface revealed that the Langmuir adsorption isotherm controls the process. Based on the quantity of free energy of adsorption observed, it was determined that there is physical contact between the OPE and the surface of SS in this experiment. It was possible to identify the most effective phytochemicals for corrosion inhibition based on the findings of quantum chemical calculations, which were subsequently evaluated in the laboratory.

electrochemistry