Abstract:In order to explore the interactional relations of internal chloride and external chloride-binding amongst the cementitious materials, the chloride-binding capacity of mortars composed of marine sand (MS) or washed marine sand (WMS) were investigated. Results indicate that more external chloride can penetrate and diffuse more deeply into the WMS mortar than that in the MS mortar. This phenomenon suggests that the external chloride migration resistance due to WMS is lower than that caused by MS. The distribution trends of the bound chloride content in the two types of mortars are the same at different immersion times. However, a significantly decreased area of the bound chloride content exists at the border of the external penetration area (EPA) and the external unaffected area (EUA) at the immersion ages of 3 and 7 d, and then it disappears gradually with immersion time. The WMS mortar can bind more external chloride, whereas the MS mortar can bind more internal chloride, at different immersion times. The distributions of bound chloride conversion rate in the EPAs of the two types of mortars differ across immersion times. The distribution firstly decreases, and then it increases at the immersion ages of 3 and 7 d. The distribution was from increase, then decreases, and increase again at the immersion ages of 28 and 56 d. The bound chloride conversion rate in the WMS mortar is affected more greatly by external chloride penetration than that in the MS mortar. The amounts of the Friedel's salt tend to increase with prolonged immersion time. Finally, the penetration of external chloride can increase the amount of fine capillary pores smaller than 100 nm in the WMSmortar exposed for 56 d in the chloride salt solution (WMS-E) specimen.

Chloride-binding capacity of mortars composed of marine sand subjected to external chloride penetration

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Chloride Binding Capacity and Its Effect on the Microstructure of Mortar Made with Marine Sand

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Chloride penetration and binding behavior in unsaturated alkali-activated slag mortars

EXPERIMENTAL STUDY ON THE CHLORIDE DIFFUSION OF CONCRETE BASED ON ITS PORE STRUCTURE

Influence of moisture condition on chloride diffusion in partially saturated ordinary Portland cement mortar

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Chloride erosion resistance of calcium formate incorporated cement mortar under chloride attack

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Experiments on Chloride Binding and Its Release by Sulfates in Cementitious Materials

Study on the chloride ion binding rate of sulfoaluminate cement mortars containing different mineral admixtures

Co-effects of initial and exposure environments on chloride penetration

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Chloride Ion Ingress Distribution Within an Alternate Wetting-Drying Marine Environment Area

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Influence of Initial Curing Conditions and Exposure Environments on Chloride Migration in Concrete Using Electrochemical Method

Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete in Marine Tidal Zone