Abstract:This study assessed the impact of calcium silicate slag (CSS), an industrial by-product of aluminum extraction from fly ash, on the reaction kinetics, compressive strength, and efflorescence of one-part sodium carbonate-activated slag (SCS). Various proportions of CSS (0%, 10%, and 20%) were used to substitute for slag. The resulting performances were evaluated through chemical shrinkage, heat liberation, compressive strength, water absorption, phase composition (XRD and TG.), microstructures (BET and BSE-EDS), and simulated efflorescence test (partially and fully immersed in deionized water). The results indicate that the CSS possesses a porous structure. The addition of CSS impairs flowability but accelerates the development of chemical shrinkage and heat liberation. The incorporation of CSS promotes the transformation of gaylussite, leading to an increase in CASH and hydrotalcite formation. Consequently, a higher compressive strength and a lower water adsorption rate are achieved. 10% CSS addition improves the splitting tensile strength of SCS under conditions of partial immersion in the efflorescence test. However, a 20% CSS substitution exacerbates the formation of efflorescence products and reduces the splitting tensile strength. These observations are associated with residual alkalis in CSS, a lower Al/Si ratio of products, and an increase in capillary pores attributed to CSS particles. This paper demonstrates the feasibility of using alkaline solid waste for slag substitution and performance regulation in SCS and reveals the underlying mechanism. The prepared CSS-SCS binder exhibits much lower energy consumption and CO2 emission than traditional cement-based material, as determined by life cycle assessment.

Chloride penetration and binding behavior in unsaturated alkali-activated slag mortars

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Chloride binding behavior of synthesized reaction products in alkali-activated slag

Chloride transport resistance of alkali-activated concrete exposed to combined chloride, sulfate and carbonation environment

Chloride Resistance and Binding Capacity of Cementitious Materials Containing High Volumes of Fly Ash and Slag

New Insights into Pore Structure and Hydraulic Conductivity of Sodium Hydroxide Alkali-Activated Slag through Advanced Modelling

Effects of Mg-based admixtures on chloride diffusion in alkali-activated fly ash-slag mortars

Factors Affecting Kinetics and Gel Composition of Alkali–Silica Reaction in Alkali-Activated Slag Mortars

Chloride Permeability of Alkali-Activated Slag Concretes after Exposure to High Temperatures

The role of CaO and MgO incorporation in chloride resistance of sodium carbonate-activated slag

Chloride Binding Capacity and Its Effect on the Microstructure of Mortar Made with Marine Sand

Chloride Ions' Penetration of Fly Ash and Ground Granulated Blast Furnace Slags-Based Alkali-Activated Mortars

Effects of Alkali Cations from Silicate Activators and Exposure Conditions on the Alkali-Silica Reaction in Alkali-Activated Slag Mortars

Investigation of effects of reactive MgO on autogenous and drying shrinkage of near-neutral salt activated slag cement

Study on the chloride ion binding rate of sulfoaluminate cement mortars containing different mineral admixtures

Understanding the impact of main seawater ions and leaching on the chloride transport in alkali-activated slag and Portland cement

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

The long-term failure mechanisms of alkali-activated slag mortar exposed to wet-dry cycles of sodium sulphate

Recent progress in understanding setting and hardening of alkali-activated slag (AAS) materials

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack