Application of Hot Isostatic Pressing in Nickel-Based Single Crystal Superalloys

Yunsong Zhao,Siliang He,Longfei Li

DOI: https://doi.org/10.3390/cryst12060805

IF: 2.7

2022-06-08

Crystals

Abstract:Hot isostatic pressing (HIP) technology can effectively reduce microstructure defects such as micropores, which are formed during solidification and hominization heat treatment, and thus further improve the high temperature performance of nickel-based SX superalloys. This paper reviews the application of HIP treatment in nickel-based SX superalloys, focusing on the dislocation-creep closure and diffusion-creep closure mechanisms and the kinetics of annihilation of micropores by HIP. The effects of different scheme on pore closure and high temperature mechanical properties are compared. The advantages and disadvantages of different schemes are summarized. In addition, the application of HIP treatment in additive manufacturing (AM) of nickel-based SX superalloys is also discussed.

materials science, multidisciplinary,crystallography

What problem does this paper attempt to address?

This paper attempts to solve the problem of micropore defects in nickel - based single - crystal (SX) superalloys during the manufacturing process. Specifically, the paper focuses on how to effectively reduce these micropores through hot isostatic pressing (HIP) technology, thereby further improving the high - temperature performance of nickel - based SX superalloys.

### Main problems:

1. **Micropore formation**:
- After casting and standard heat treatment, there are mainly two types of micropores in nickel - based SX superalloys:
- **S - pores**: Micropores formed during dendritic solidification, mainly caused by two reasons:
1. The interdendritic liquid phase is isolated by the completely solidified dendrite trunks, resulting in volume shrinkage and inability to supplement other liquid phases, thus forming irregular micropores in the interdendritic regions.
2. The presence of partially dissolved gases during solidification forms spherical pores after solidification.
- **H - pores**: Micropores formed during the homogenization heat treatment, mainly due to the diffusion of dendrite - enriched elements (such as W, Re, Cr, Co) to the interdendritic regions, and the diffusion of interdendritic - enriched elements (such as Al, Ta) to the dendrite trunks, resulting in the Kirkendall effect and forming spherical solution pores of about several micrometers.

2. **Micropore elimination**:
- Although S - pores and H - pores can be reduced by optimizing the parameters of directional solidification and homogenization heat treatment, only HIP treatment can completely remove these micropores. HIP achieves the elimination of micropores through the combined effect of high temperature and high pressure.
- Studies have shown that the HIP temperature has a significant impact on the micropore elimination efficiency. When it is lower than the γ′ - solidus temperature, due to the hardening effect of the γ′ phase, the micropore elimination efficiency is low; while when it is higher than the γ′ - solidus temperature, the initial porosity can be almost completely eliminated.

3. **Different HIP treatment schemes and their effects**:
- The paper compares the effects of different HIP treatment schemes on micropore elimination and high - temperature mechanical properties, and summarizes the advantages and disadvantages of each scheme. For example, some studies tend to conduct HIP treatment after casting, while others conduct HIP treatment after homogenization. Recently, an integrated HIP heat treatment method has also been developed, which utilizes the rapid quenching rate provided by HIP equipment.

### Goal:

By reviewing the application progress of HIP treatment under different schemes, promote the research and development of HIP technology in the field of nickel - based SX superalloys, and ultimately improve the high - temperature and mechanical properties of these materials.