Abstract:In this paper, 2 atom % Al-doped ZnO (AZO) was prepared by the co-precipitation method together with sparking plasma sintering (SPS) treatment. The as-synthesized AZO powders show the morphology of hollow hexagonal towers, which result in a high porosity of 50.6% in the bulk sample consolidated by SPS sintering at 400 °C, and the porosity decreases gradually with increasing sintering temperature up to 1000 °C. Positron annihilation measurements reveal that even after sintering at 1000 °C, there are still a considerable number of small pores. A high electrical conductivity of 3 × 105 S m–1 is achieved at room temperature for the AZO sample sintered at 1000 °C, while the absolute values of Seebeck coefficient keep at relatively high values between 59 and 144 μV K–1 in the measurement temperature range of 27–500 °C, leading to a high power factor of 3.4 × 10–3 W m–1 K–2. On the other hand, the pores in AZO act as strong phonon scattering centers, and an extremely low thermal conductivity of 1.5 W m–1 K–1 measured at room temperature is obtained for AZO sintered at 400 °C. Due to the residual pores in the 1000 °C-sintered sample, the thermal conductivity is still relatively low. As a result, a maximum ZT of 0.275 measured at 500 °C is obtained in this sample, which is the highest ZT reported for ZnO around this temperature.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c16506?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c16506</a>.Thermal gravity analysis for the Al-doped ZnO (Figure S1), TEM images of Al-doped ZnO sintered at different temperatures (Figure S2), and structural characterization and thermoelectric properties of undoped ZnO prepared by co-precipitation combined with SPS treatment (Figures S3–S5) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c16506/suppl_file/am0c16506_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Microstructure and thermoelectric properties of Al-doped ZnO ceramic prepared by spark plasma sintering

Microstructure and thermoelectric properties of Zn1−xAlxO ceramics fabricated by spark plasma sintering

Preparation and thermoelectric properties of Al2O 3-doped ZnO ceramics

Optimization of thermoelectric properties of Al-doped Zn1−xAlxO under high pressure and high temperature

Microstructure and thermoelectric properties of α-and γ-Al2O3 doped ZnO under high pressure

Preparation and Thermoelectric Properties of Al<sub>2</sub>O<sub>3</sub>-Doped ZnO Ceramics

Significant Enhancement in the Thermoelectric Performance of Aluminum-Doped ZnO Tuned by Pore Structure

Thermoelectric Properties and Electronic Structure of Al-Doped Zno

Defects and microstructure of highly conducting Al-doped ZnO ceramics obtained via spark plasma sintering

Processing and enhancement of thermoelectric performance of Nb doped ZnO (NZO) ceramics

High Dielectric Constant in Al-doped ZnO Ceramics Using High-Pressure Treated Powders

High Thermoelectric Performance of ZnO by Coherent Phonon Scattering and Optimized Charge Transport

Enhanced Al/Ni Co-Doping and Power Factor in Textured ZnO Thermoelectric Ceramics Prepared by Hydrothermal Synthesis and Spark Plasma Sintering

Microstructure and Electrical Properties of Al-doped ZnO Thin Films

Thermoelectric Properties and Microstructure of (zn0.98al0.02)o Prepared by MA/HP Process

Thermal conductivity suppression in ZnO with AlZn 2 O 4 and ZnP 2 for thermoelectric applications

Record‐High Thermoelectric Performance in Al‐Doped ZnO via Anderson Localization of Band Edge States

Influence of Core-Shell Structure on Thermoelectric Properties of Zn0.98Al0.02O

Synergistic optimization of the thermoelectric properties of Zn0.98Al0.02O using high-pressure and high-temperature treatment

Thermoelectric Performance of Zn and Ge Co-Doped In2o3 Fine-Grained Ceramics by the Spark Plasma Sintering

Thermoelectric Performance of Zn and GeCo-Doped In2O3 Fine-Grained Ceramics by the Spark Plasma Sintering