Synthesis of core-shell ZIF-8@α-Fe2O3 nanorods and improvement of selectivity for ammonia gas

Qin Ye,Caiyun Liu,Jinan Li,Haiying Wang,Shihang Yan,Mingyue Meng,Hongyan Xu

DOI: https://doi.org/10.1016/j.snb.2022.132134

2022-09-15

Abstract:Uniform and dense α-Fe2O3 nanorods were directly synthesized on the ceramic tube substrate by hydrothermal method, and then a layer of porous and dense ZIF-8 film was hydrothermally grown and coated on the surface of α-Fe2O3 nanorods after immersion in ligand solution and high-temperature treatment. Then the core-shell ZIF-8 @ α-Fe2O3 nanorods were obtained. The elements, composition, surface morphology, and crystal structure of the samples were analyzed by XPS, SEM, TEM, and XRD. These results indicate that the width of the rod-shaped α-Fe2O3 was between 20 and 40 nm while the rod-shaped α-Fe2O3 coated with a layer of dense porous ZIF-8 was between 50 and 80 nm. The gas sensing results reveal that compared with pure α-Fe2O3 nanorods, ZIF-8 @ α-Fe2O3 had a great improvement in gas selectivity (11.7), response value (136.9 for ammonia gas of 50 ppm at 280 °C). The working process and gas sensing mechanism of the ZIF-8 @ α-Fe2O3 were discussed and it demonstrates that ZIF-8 not only plays a screen role in the gas-sensitive response process, but also increases the sensitivity by adsorbing oxygen molecules. It proved that the direct growth of ZIF-8 @ α-Fe2O3 on the ceramic tube provides a more effective way to improve the gas response and selectivity.