Abstract:The work scientifically substantiates the use of an effective technology for increasing the wear resistance of cylindrical parts, using the example of protective sleeves of cantilever pumps, due to electromechanical surface hardening. A review of research was carried out and it was established that the achievement of the highest values of microhardness of the surface layer at a depth of up to 1.2 mm is possible during electromechanical processing of protective sleeves of cantilever pumps. The application of various modes and schemes of electromechanical surface hardening (EMSH) is accompanied by a change in structure and, as a result, an increase in the hardness of the surface layer of the bushings. The actual contact area of the tool roller with the processed surface and the depth of the temperature-deformation effect depend on the physical and mechanical properties of the materials and the pressing force. The formation of a temperature gradient in the hardened zone at a depth of up to 1.2 mm from the surface has been proven. Metallographic analysis of the surfaces of the sleeves treated by EMSH shows the formation of a white layer with reduced etchability and increased hardness in the hardening zones. The results of the X-ray structural analysis confirmed the formation of the martensite phase in the hardening zone. The microhardness of the hardened steel zone increased by 2.6...3.6 times compared to the initial values at a depth of up to 1 mm from the surface, depending on the materials. In the case of their overlap, the alternation of a fully hardened zone, a partially hardened zone, and a self-relief zone is observed. At the same time, the microhardness of steels along the surface depends on the hardening scheme. Wear tests under friction conditions of parts of cantilever pumps paired with stuffing boxes showed that the wear resistance of protective sleeves after EMSH increased by 3.1 times for 45 steel, 1.9 times for U8 steel, 2.5 times for SHKH15 steel, for cast iron by 1.9 times compared to the initial values. The use of U8 steel samples after EMSH, instead of serial bushings made of steel 45, allows to increase the wear resistance of parts by 6.1 times, which allows us to recommend U8 steel for use in the manufacture of protective bushings for console pumps. On the basis of the research, recommendations are given for the application of EMSH for the formation of a surface layer with increased wear resistance of protective sleeves during their production and during repair of console pumps in workshops or service centers of agribusiness companies.

Improving the Wear Resistance of Key Components in a Sandvik Crusher by Applying a Hybrid Coating

Application of Magnetron Sputter Ion Plated CrAlTiN Composite Coating in Improving Wear Resistance of Milling Cutter

Design for Manufacturing of Cemented Carbide Coated Components Toward High Wear and Impact Resistance Performance

Improving Wear Resistance of Agricultural Machine Components by Applying Hard-Alloy Thick-Layer Coatings Using Plasma Surfacing

Influence of the chemical composition of the material and the physical and mechanical properties of the coating on the wear resistance of the "shaft — coating — bearing bush" tribological coupling

Wear Resistance and Anti-Friction of Expansion Cone with Hard Coating

Abrasion Resistance of Restorative Coatings for Crankshafts and Bearings in Agricultural Machinery

Crack and Wear Resistance of Hard Coatings

Wear of Throwing End of Vertical Shaft Impact Crusher

To the question of improving the wear resistance of high manganese steel castings

CAVITATION EROSION BEHAVIOR OF WC–Co COATINGS ON TURBINE STEEL DEPOSITED BY COLD SPRAY

Wear resistance of a Metco 1030A hard coating deposited on Hadfield steel by laser cladding for ore comminution application

Assessment of Hydroabrasive Wear Resistance of Construction Materials with Functional Coatings, which are Formed by Resource-Saving and Environmentally Friendly Technologies

Structure and Abrasive Wear Resistance of Stainless-Steel Surface Layers Alloyed with Boron

Surface modification technologies for enhancing the tribological properties of cemented carbides: A review

Diamond grits reinforced coating on 35CrMnSi coal shearer cutting teeth: Microstructure, wear resistance and service performance in coal extraction

Improving Abrasive Wear Resistance for Steel Hardox 400 by Electro-Spark Deposition

Effect of Hard Chroming on Wear Loss of Rotavator Blade

Wear Law and Parameter Optimization Study on the Split Cone of a Vertical Shaft Impact Crusher

Raising the Wear Resistance of Chromium-Nickel Steel Surface-Hardened with Titanium Carbide Particles

Study of Wear Resistance of Cylindrical Parts by Electromechanical Surface Hardening