Effect of feedstock bimodal powder design and cold isostatic pressing on the mechanical behavior of binder jetting additive manufactured Inconel 718 superalloy
Wenxin Yang,Zhicheng Cai,Wei Duan,Xin Deng,Tao Lin,Zhiren Chen,Fuyuan Xie,Jinyang Liu,Zhi Qu,Feng Jin,Li He
DOI: https://doi.org/10.1016/j.jmapro.2024.11.085
IF: 5.684
2024-12-06
Journal of Manufacturing Processes
Abstract:Densification of metallic and ceramic materials within the context of binder jetting additive manufacturing (BJAM) presents a considerable technical challenge. This study leveraged a bimodal feedstock powder design, in conjunction with cold isostatic pressing (CIP), to optimize the green density of BJAMed Inconel 718 (IN718) superalloy. This approach consequently elevated the sintered density and the attendant mechanical properties to their highest potential. Supplementary to this, a pair of heat treatment methodologies were executed: a solid solution-dual aging process (HT-1) and a dual aging process (HT-2), aimed at augmenting the mechanical properties of the alloy. The investigation revealed that the bimodal feedstock powder configuration, with a 10:1 mass ratio of coarse to fine particles (D 50 29.1 μm and D 50 11.4 μm, respectively), outperformed the unimodal powder design regarding relative density, dimensional precision, and mechanical integrity. Furthermore, the CIP process was identified as an essential step for enhancing the relative density and mechanical behavior of the BJAMed IN718 superalloy. The synergistic effect of the bimodal powder design and CIP treatment significantly improved densification, achieving a relative density of 98 %, and enhanced mechanical properties, with an ultimate tensile strength reaching 1105 MPa, even under the conditions of a relatively low sintering temperature of 1285 °C and a brief dwell time of 60 min. When juxtaposed with the as-sintered and HT-2 treated IN718 samples, the HT-1 treated IN718 displayed a finer grain structure within the γ matrix, which translated to superior mechanical properties, with an ultimate tensile strength of 1206 MPa.
engineering, manufacturing