Fabrication and Characteristics of Poly(benzimidazole/fluoro/ether/siloxane/amide)/Sulfonated Polystyrene/Silica Nanoparticle-Based Proton Exchange Membranes Doped With Phosphoric Acid

Ayesha Kausar

DOI: https://doi.org/10.1080/00914037.2014.936589

2014-10-27

International Journal of Polymeric Materials and Polymeric Biomaterials

Abstract:Novel poly(benzimidazole/fluoro/ether/siloxane/amide) (PBFESA) was developed for the formation of hybrid proton exchange membrane. Afterward, phosphoric acid doped PBFESA/PS-S/SiNPs was prepared with PBFESA, sulfonated polystyrene (PS-S), and 0.1–2 wt% silica nanoparticles (SiNPs). Tensile strength of acid doped PBFESA/PS-S/SiNPs nanocomposites increased from 63.9 to 68.1 MPa with increasing SiNPs loading. They had higher ion exchange capacity (IEC) of 2.3–3.3 mmol/g and proton conductivity of 1.9–2.7 S/cm at 80°C (higher than perfluorinated Nafion 117 membrane 1.1 × 10−1 S/cm). A H2/O2 fuel cell using PBFESA/PS-S/SiNPs 2 (IEC 3.3 mmol/g) showed better performance than Nafion 117 at 40°C (30% RH).