Abstract:Silicon is considered as a promising candidate of the anode material for the next generation lithium-ion batteries, due to its substantially higher gravimetric and volumetric capacity compared to conventionally used graphite. Electrolyte additives, fluoroethylene carbonate (FEC) and vinylene carbonate (VC) particularly, are usually applied for silicon-based lithium-ion batteries to tackle the problems such as poor capacity retention and low coulombic efficiency.1-3 In the present work, the decomposition mechanism of FEC as well as the surface modification of Si electrodes were investigated.4 It was observed that the FEC additive degrades at a higher reduction potential prior to the other carbonate solvents. A conformal solid electrolyte interphase (SEI), which consists of the decomposition products of FEC, is instantaneously formed on the silicon electrode as a result. This stable SEI layer sufficiently limits the emergence of cracks and suppresses the additional SEI formation from the decomposition of other electrolyte components. Both of these effects lead to a slower increase in polarization, thus a slower capacity fading, for the FEC containing cell. The differences in the SEI layer, formed with or without the presence of FEC, are schematically demonstrated in Fig 1. Besides, it was also observed that the LiPF6 decomposition can be influenced with the presence of FEC, and this was further studied with a combination of X-ray photoelectron spectroscopy (XPS) and solid-state nuclear magnetic resonance (NMR) techniques. We also demonstrated that by forming an effective SEI layer with the FEC and VC electrolyte additives, the silicon electrodes can be equally well functioning with a novel lithium 4,5-dicyano-2-(trifluoromethyl)imidazolide (LiTDI)-based electrolyte as with the state-of-art LiPF6-based electrolyte.5 Figure 1

Dealloying of modified Al-Si alloy to prepare porous silicon as Lithium-ion battery anode material

Scalable and Low-Cost Synthesis of Porous Silicon Nanoparticles As High-Performance Lithium-Ion Battery Anode

Scalable Preparation of Porous Silicon Nanoparticles and Their Application for Lithium-Ion Battery Anodes

Porosity Controlled Synthesis of Nanoporous Silicon by Chemical Dealloying As Anode for High Energy Lithium-Ion Batteries.

Large-scale Fabrication, 3D Tomography, and Lithium-Ion Battery Application of Porous Silicon.

Scalable Synthesis of Porous Silicon by Acid Etching of Atomized Al-Si Alloy Powder for Lithium-Ion Batteries

A porous silicon anode prepared by dealloying a Sr-modified Al–Si eutectic alloy for lithium ion batteries

Porous Si/Fe<sub>2</sub>O<sub>3</sub> Dual Network Anode for Lithium-Ion Battery Application

Scalable Synthesis of Porous SiFe@C Composite with Excellent Lithium Storage.

Scalable Fabrication of Micro-Sized Bulk Porous Si from Fe–Si Alloy As a High Performance Anode for Lithium-Ion Batteries

Dual network porous Si/Al9FeSi3/Fe2O3 composite for high performance Li-ion battery anode

Porous Si/Fe2O3 Dual Network Anode for Lithium–Ion Battery Application

Facile preparation of silicon/carbon composite with porous architecture for advanced lithium-ion battery anode

Improving Electrochemical Performance of Thick Silicon Film Anodes with Implanted Solid Lithium Source Electrolyte

Reversible Silicon Anodes Enabled by Fluorinated Inorganic-Organic Hybrid Coating

Boosting the anode performance of the porous Si coated with polydopamine and cross-linked with sodium alginate

Solution synthesis of porous silicon particles as an anode material for lithium ion batteries.

Atomic/Molecular Layer-Deposited Laminated Li2O-Lithicone Interfaces Enabling High-Performance Silicon Anodes.

Understanding the Roles of Electrolyte Additives on the Surface Modification Mechanism of Silicon-Based Anodes in Lithium-Ion Batteries

Surface Modification of Micro-Silicon Anode for High-performance Lithium-Ion Batteries

Silicon Foam Anode with Stabilized Interface for Lithium-ion Batteries