Core-Shell Emulsion Copolymerization and Characterization of Polysiloxane Bearing Vinylic Function/Acrylate Monomer
Zhu Zhikai,Shen Zhiwei,Luo Dan,Li Jinchun,Chen Qiang
DOI: https://doi.org/10.3969/j.issn.0253-4312.2013.06.003
2013-01-01
Abstract:A macromolecular vinyl siloxane monomer,methacryloxyethyl polymethyl-hydrosiloxane ether(MEPMHSE) has been synthesized based on polymethyl-hydrosiloxane(PMHS) and 2-hydroxyethyl methacrylate(HEMA).The core-shell polyacrylate particles,with the average size of 135.2 nm and narrower particle size distribution(PDI=0.045),was synthesized by core-shell emulsion polymerization method,in which methyl methacrylate(MMA),butyl acrylate(BA) were used as main monomers,methacryloxyethyl polymethylhydrosiloxaneether(MEPMHSE) is added as polyacrylate modifier.The resulting silicone-containing monomer was characterized by FT-IR,1HNMR,the structure and size of the latex particles were characterized by TEM,DSC and Nanometer laser particle size and zeta potential analyzer.The effect of the mass ration of emulsifier formulation,emulsion content and silicone monomer content on the stability of emulsion;the water absorption of latex film;gelatin rate on reaction and film of hydrophobic were discussed separately.The experiment showed that the hydrophobicity of silicone monomer modified acrylate was much better than regulate acrylate.The water-drop and the silicone modified acrylate latex film surface's angel contact,compared with 65°of free-silicone acrylate latex,surpassed 98°with the silicone monomer usage amount of 6%.