Abstract:The polysiloxane/acrylates copolymer latex with core-shell structure was prepared in the semi-batch emulsion polymerization of methyl methacrylate (MMA) in the presence of polysiloxane latex as seeds. The polysiloxane seeded latex was polymerized by octamethylcyclotetrasiloxane (D-4) and vinyl rnethylcyclotetrasiloxane (ViMeSiO)(4), and methyl triethoxysilane (MTES) as the crosslinking reagent. The effects of polymerization methods and preparation conditions (the concentrations of emulsifier and initiator, the adding mode and rate of MMA) on the average particle size, and its distribution, and the morphology of the obtained particles were studied. In comparison with batch process, the semi-batch process by adding MMA is more preferable for preparing a stable copolymer latex with smaller particle size and narrower distribution. The higher concentration of emulsifier and initiator will cause smaller particle size and narrower particle size distribution, the faster adding rate of MMA will cause smaller particle size, but wider particle size distribution. The TEM photos show that the composite particles prepared in the semi-batch process by adding MMA monomers have clear core/shell structure, but particles by batch method have irregular shape and no such structure. Besides the micelle nucleation during the seeded emulsion polymerization, the homogeneous nucleation can't be neglected because of the slight solubility of MMA in water. Under lower concentration of emulsifier and slower adding rate of MMA, the polymerization of, shell monomers will be restricted in the "transition area" on the surface of the polysiloxane seeds. The particle size, distribution and morphology of the composite particles can be controlled by changing the concentration of the emulsifier and the adding rate of MMA.

Preparation of Polyacrylate - Polysiloxane Core - Shell Latex Particles

Seed Semicontinuous Emulsion Multi-Copolymerization of (meth)acrylates with High-Solid Content - Effect of the Operation Conditions

Synthesis and properties of alkoxysilane-modified acrylic latex via miniemulsion polymerization

A Novel Method for Preparing Click-Ready Latex and Latex with Stability Against High Electrolyte Concentrations

Particle Size Distribution and Its Formation Mechanism of Polysiloxane/Acrylates Core-Shell Composite Particles

Preparation and Properties of Silicone-Acrylate Copolymer Latex

Synthesis of Silicone-Acrylate Copolymer Latexes and Their Film Properties

Core-Shell Emulsion Copolymerization and Characterization of Polysiloxane Bearing Vinylic Function/Acrylate Monomer

Synthetic methods of acrylate polymer latexes modified with organosilicons and their film properties

Anchoring of polyacrylate onto silica and formation of polyacrylate/silica nanocomposite particles via in situ emulsion polymerization

Morphological prediction and its application to the synthesis of polyacrylate/polysiloxane core/shell latex particles

Properties and Characterization of Novel Cationic Polyacrylate Latex Containing Fluorine and Silicon Prepared with Soap-Free Emulsion Polymerization

SYNTHESIS, CHARACTERIZATION AND CROSSLINKING REACTION OF REACTIVE COMPOSITE LATEX

Preparation and characterization of self-crosslinking acrylate emulsion modified by divinyl silane

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Core-Shell Morphology Prediction Via Interfacial Energy Estimation and Its Application to Polyacrylates-Polysiloxane Latex Particles.

A Novel Approach to Prepare Core/shell Polymer Latex Particles with High Sulphonate Contents

Synthesis and properties of soap-free poly(methyl methacrylate-ethyl acrylate-methacrylic acid) latex particles prepared by seeded emulsion polymerization

Synthesis and Properties of Novel Fluorinated Cationic Polymer Latex

Preparation and Structure Control of Hollow Polymer Particles——Synthesis and Effect on the Hollow Structure of the Core Latex

Preparation and Thermal Stability of Phosphorus Acrylic Latex Modified with Organic Silicon