Abstract:Iron red, a traditional Jingdezhen overglaze color, is primarily colored with iron oxide (Fe2O3). In traditional processes, the main ingredient for the iron red overglaze color, raw iron red, is produced by calcining iron vitriol (FeSO4·7H2O). Analysis of ancient iron red porcelain samples indicates that the coloration is unstable, ranging from bright red to dark red and occasionally to black. Addressing this, the present study, from a ceramic technology standpoint, conducts a series of calcination experiments on industrial iron vitriol at varying temperatures. Utilizing methodologies such as differential scanning calorimetry-thermogravimetry (DSC-TG), Raman spectroscopy, X-ray diffraction (XRD), scanning electron microscopy with X-ray energy dispersive spectrometry (SEM-EDS), and optical microscopy (OM), this research scientifically explores the impact of iron vitriol's calcination temperature on the coloration of traditional Jingdezhen iron red overglaze color. The findings indicate that from room temperature to 550 °C, the dehydration of iron vitriol resulted in the formation of Fe2(SO4)3 and a minimal amount of α-Fe2O3, rendering the iron red overglaze color a yellowish-red shade. At 650 °C, the coexistence of Fe2(SO4)3 and α-Fe2O3 imparted a brick-red color to the iron red. As the temperature was elevated to 700 °C, the desulfurization of Fe2(SO4)3 produced α-Fe2O3, transitioning the iron red to an orange red. With further temperature increase to 750 °C, the particle size of α-Fe2O3 grew and the crystal reflectivity decreased, resulting in a purplish-red hue. Throughout this stage, the powder remained in a single α-Fe2O3 phase. Upon further heating to 800 °C, the crystallinity of α-Fe2O3 enhanced, giving the iron red overglaze color a dark red or even black appearance.

Effect of Annealing Temperature of Brownish-Red Pigment Based on Iron Oxide Extracted by Hydrothermal Route from Mill-Scale Steel Slag

Novel red composite pigment with high thermostability from iron ore tailings: Synthesis and coloring mechanism

Synthesis and Characterization of Red Pigment from Acid Regeneration Plant (ARP) By-product Via Rod Milling Process

Sustainable reutilization of ion-adsorbed rare earth tailings: Preparation of low-cost functionalized pigments

An Environmentally Friendly Method for Producing α-Fe2O3 Pigment from Low-Grade Hematite Residue

Experimental Study on the Preparation of High-Purity Iron Oxide Red by Acid Leaching Iron from Coal Gangue

Studies of the Morphology of Hematite Synthesized from Waste Iron Sulfate

Preparation of Iron Oxide Red with High Titanium Slag Recovery Dust

Colour Change of Red Iron Oxide by One-step Method Using Oxidant

Novel environment friendly inorganic red pigments based on attapulgite

Production of brown and black pigments by using flotation waste from copper slag

Reductive Smelting of Neutralized Red Mud for Iron Recovery and Produced Pig Iron for Heat-Resistant Castings

Hydrometallurgical Processing of Brazilian Iron Ore Tailings for the Synthesis of Pigments

Synthesis and characterization of iron oxides and their application as inorganic pigments in white paint

Reducing Iron Oxide with Ammonia: A Sustainable Path to Green Steel

Mixed oxides with corundum-type structure obtained from recycling can seals as paint pigments: color stability

An overview of using solid wastes for pigment industry

Study on the Influence of Calcination Temperature of Iron Vitriol on the Coloration of Ancient Chinese Traditional Iron Red Overglaze Color

Pilot-scale process to produce bio-pigment from Monascus purpureus using broken rice as substrate for solid-state fermentation

Influence of Reduction Temperatures on Reduction of FeO-Containing Slag by Agricultural Waste

Experiments on effect of red mud-based slag on distribution of sulfur in liquid iron