Long-term effect of recycled aggregate on microstructure, mechanical properties, and CO2 sequestration of rendering mortars
Artur Spat Ruviaro,Laura Silvestro,Fernando Pelisser,Afonso Rangel Garcez de Azevedo,Paulo Ricardo de Matos,Antônio Luiz Guerra Gastaldini
DOI: https://doi.org/10.1016/j.conbuildmat.2022.126357
IF: 7.4
2022-02-01
Construction and Building Materials
Abstract:This study aimed to investigate the effect of replacing 30% natural fine aggregate with recycled aggregate (RA) produced from construction and demolition waste (C&DW) on the long-term properties of Portland cement rendering mortars. For this purpose, mortars were produced using natural aggregate (REF), crushed recycled aggregate (CRA), and sieved crushed recycled aggregate (CSRA). The mortars were applied as external coating, and properties such as their adhesion, compressive and flexural strengths were evaluated, as well as their microstructure using X-ray diffraction (XRD), thermogravimetric analysis (TGA), and Fourier transform infrared spectroscopy (FTIR) after 1,059 days of exposure. Visual surface analysis was performed on the external coating to identify the cracking. After 1,059 days of exposure, the CRA and CSRA mortars showed adhesion strength statistically equal to REF and significantly higher than the minimum values established by standard for internal and external coatings. Regarding 1,059-day compressive and flexural strengths, respective increments of 39 and 42% were observed for the CRA composition compared to REF. No cracks were observed in any of the mortars after 1,059 days. Furthermore, the CO2 assessment indicated net CO2 emission reductions of 59 and 38% for CSRA and CRA, respectively, compared to REF. Overall, the incorporation of RA resulted in mortars with superior long-term mechanical properties and a significantly lower net CO2 emission than the mortar with natural aggregate.
construction & building technology,materials science, multidisciplinary,engineering, civil