Hydrogen purification by Mg alloy hydrogen adsorbent

Haiguang Wang,Yongfeng Liu,Jun Zhang

DOI: https://doi.org/10.1007/s10450-021-00348-2

2022-01-21

Adsorption

Abstract:Metal hydrides are promising hydrogen storage materials. Their extraordinary hydrogen adsorption capacity and selectivity make them ideal adsorbents for hydrogen purification. In particular, Mg-based materials demonstrate ultrahigh adsorption capacity and the starting materials are widely available. However, the utilization of metal hydrides in gas purification is limited due to surface poisoning which accounting for reduction on H2 adsorption. In this study, fluorinated MgNi0.1Fe0.05Ti0.05 alloy was proposed and synthesized by vacuum induction melting and impregnation method. At 300 °C, when the H2 partial pressure was 1.0 MPa, the adsorption capacity was up to 25 mmol/g. However, for the alloy without fluorination treatment, the adsorption capacity decreased sharply after the exposure to CO2 and CO, while the fluorinated sample still kept considerable adsorption capacity. In cyclic breakthrough experiments, the breakthrough time did not decrease over multiple experimental runs for the fluorinated samples. The adsorbent successfully separated H2 from CO2 when the CO2 and CO concentration was up to 50% and 100 ppm respectively. A bench scale test was conducted on a one-bed vacuum pressure swing adsorption apparatus to verity the feasibility of warm hydrogen purification technology using fluorinated MgNi0.1Fe0.05Ti0.05 adsorbent. The hydrogen in the warm mixed gas (30% H2 + 70% CO2) was captured and purified. The hydrogen recovery rate reached 95% while the purity was 95.1%. This study demonstrated one promising method for direct hydrogen separation, which could be possibly applied for separating hydrogen from carbonaceous gas mixtures.

English Else