Salicylaldehyde-assisted ZrO 2 -induced conversion approach to prepare high performance hollow fiber-supported UiO-66-NH 2 membrane for hydrogen separation
Yi Liu,Lu Liu,Yifan Yang,Tengfei Yang,Claudia Li,Sibudjing Kawi,Xiaobin Wang
DOI: https://doi.org/10.1016/j.memsci.2023.121851
IF: 9.5
2023-06-16
Journal of Membrane Science
Abstract:The efficient separation of hydrogen from mixtures is essential to enable its widespread use as an alternative energy source to fossil fuel. UiO-66-NH 2 membrane presents attractive application prospects in hydrogen purification. However, the cost-effective synthesis of UiO-66-NH 2 membrane with high reproducibility, scalability, and stability remains a challenge. Herein, we developed a ZrO 2 -induced approach to prepare UiO-66-NH 2 membrane supported on α-Al 2 O 3 hollow fiber (HF). Commercial ZrO 2 powders were first uniformly introduced onto the HF via a simple rotating method, followed by directly inducing the growth of well-intergrown UiO-66-NH 2 membrane layer through these ZrO 2 powders. The samples were well characterized by various physicochemical analysis techniques like SEM, EDX, XRD, N 2 adsorption/desorption, CO 2 adsorption, XPS, ATR-FTIR, etc. The pore aperture of UiO-66-NH 2 membrane treated with salicylaldehyde (P-UiO-66-NH 2 ) was reduced to 0.37 nm, which was slightly smaller than the kinetic diameter of CH 4 (0.38 nm). Consequently, P-UiO-66-NH 2 membrane demonstrated a promising H 2 /CH 4 ideal selectivity of 21.7, which was superior to other related reports. The gas permeances of P-UiO-66-NH 2 membrane were almost constant with the trans -membrane pressure difference, demonstrating that the membrane was compact and absent of pinholes. The membrane exhibited good thermal stability during the entire 80-h run between 30 °C and 200 °C with an average separation factor of 19.2–23.3 for binary H 2 –CH 4 mixture. The membrane additionally presented good hydrothermal stability, mechanical strength and reproducibility. We believed that the developed preparation strategy has high potential in the development of UiO-66-NH 2 membrane with high performance.
engineering, chemical,polymer science