Preparation and characterization of small-size amorphous MOF mixed matrix membrane

Zibo Yang,De Ao,Xiangyu Guo,Lei Nie,Zhihua Qiao,Chongli Zhong

DOI: https://doi.org/10.1016/j.seppur.2021.118860

IF: 8.6

2021-10-01

Separation and Purification Technology

Abstract:<p>In recent years, amorphous metal-organic frameworks (AMOFs) with original structural units but no long-range ordering have attracted much attention. However, AMOFs with abundant open metal sites (OMSs) have seldom been applied for gas separation membranes mainly attributed to poor membrane-forming property caused by large particle sizes. In this work, we proposed the method of polymer induction for the first time to obtain small-sized AMOFs particles with stronger alkaline stability, higher hydrophilicity and better CO₂/N₂ adsorption selectivity than crystal, which were applied to mixed matrix membranes (MMMs) as filler, exhibiting good separation performance. First, polyethyleneimine (PEI) was used as an inducer to obtain small-sized UiO-66-NH₂ particles (SU-1) and improve the membrane-forming property. Additionally, we adopted a thermal-treatment method to treat the particles and obtained an amorphous SU-1 (ASU-1). Furthermore, MMMs were prepared by uniformly mixing ASU-1 filler with strong basic polymer polyvinylamine (PVAm), and the prepared MMMs showed the optimal CO₂ separation performance at an ASU-1 loading of 28.5 wt%, with a CO₂/N₂ selectivity of 71.33 at 1.5 bar and a CO₂ permeance of 721 GPU, which was much higher than the MMM using pristine PVAm and SU-1. This study provides a promising strategy for preparing high-performance MMMs through decreasing particle size and increasing the separation performance of MOF fillers.</p>

engineering, chemical

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to improve the CO2/N2 separation performance by preparing small - sized amorphous metal - organic frameworks (AMOFs) mixed - matrix membranes (MMMs) in gas - separation membrane materials. Specifically, the paper focuses on the following points:

1. **Improving the stability of membrane materials**: Traditional metal - organic frameworks (MOFs) are unstable in alkaline environments, which limits their use in practical applications. The paper proposes a method to solve this problem by preparing amorphous MOFs (AMOFs) with higher alkali - stability through polymer induction and heat treatment.

2. **Improving the film - forming performance of membrane materials**: Large - sized MOFs particles can cause defects in the membrane materials during the preparation process, affecting the separation performance. The paper prepared small - sized MOFs particles (SU - 1) by the polyethyleneimine (PEI) induction method, and further converted them into amorphous state (ASU - 1) through heat treatment, improving the film - forming performance of the membrane materials.

3. **Enhancing the CO2/N2 adsorption selectivity of membrane materials**: The paper prepared high - performance MMMs by uniformly mixing the prepared amorphous MOFs (ASU - 1) as fillers with the strongly alkaline polymer polyvinylamine (PVAm). The experimental results show that when the loading amount of ASU - 1 is 28.5 wt%, the selectivity of CO2/N2 of the prepared MMMs reaches 71.33 at an inlet pressure of 1.5 bar, and the CO2 permeability is 721 GPU, which is significantly higher than that of pure PVAm membranes and MMMs with other fillers.

4. **Optimizing the interface compatibility of membrane materials**: The paper enhanced the interface compatibility between the polymer and the filler by improving the surface hydrophilicity of the PSf - supported membrane, thereby reducing the defects in the membrane materials and improving the separation performance.

In conclusion, through a series of innovative methods, this paper successfully prepared amorphous MOFs mixed - matrix membranes with excellent CO2/N2 separation performance, providing new ideas for the design and preparation of membrane materials with high separation performance.