Abstract:Nanoparticles of Co 0.5 Cd 0.5 Fe 2 O 4 have been fabricated using a typical sol–gel combustion technique. X-ray diffraction (XRD), field emotion-scanning electron microscopy (FE-SEM), energy dispersive spectroscopy, Raman spectroscopy and vibrating sample magnetometer measurements were used to study the structure, morphology and magnetic characteristics of ferrite nanoparticles at varied calcination temperatures. The electrical characteristics of the structure are calculated from the first principles using the GGA approach in density functional theory. The X-ray analysis of calcined samples revealed the formation of the spinel fcc crystalline phase was unaffected by the increment in calcination temperature. Due to the presence of cubic cadmium oxide (CdO), several low-diffraction peaks with the symbol * are present. As calcination temperature rises, the average crystal size increases from 20.34 to 21.94 nm. The FE-SEM images indicated a porosity structure and agglomerations caused by the interaction of uniform magnetic nanoparticles. The compositional analysis of the Co 0.5 Cd 0.5 Fe 2 O 4 sample reveals the existence of desired constituents and the elimination of all undesirable precursors. Raman spectroscopy proved spinel ferrite nanoparticles include tetrahedral (A) sites and octahedral (B) sites. The magnetic hysteresis curves demonstrate the ferromagnetic nature, and it was observed that calcination temperatures significantly impacted the magnetic characteristics. As calcination temperature increased, saturation and remanence magnetization decreased, and inter-sub-lattice (A–B) super-exchange interactions were slightly more pronounced in smaller particles than in larger ones. Coercivity increases as calcination temperature rises. This can be attributed to the increase in particle size within the singular domain region. In addition, theoretical results (band structures) indicate that cobalt-cadmium ferrite possesses half-metallic properties.

Conventional versus microwave combustion synthesis of CoFe2O4 nanoparticles

Combustion Synthesis and Magnetic Investigation of Nanosized CoFe2O4

Characterization and magnetic properties of CoFe2O4 nanoparticles synthesized by the co‐precipitation method

Novel Preparation and Physicochemical Characterization of a Nanocrystalline Cobalt Ferrite System

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Chemical synthesis and magnetic properties of monodisperse cobalt ferrite nanoparticles

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Synthesis and Characterization of Cobalt Ferrite through Co-Precipitation Technique

Study of CoFe2O4/CoFe2 nanostructured powder

Preparation and Characterization of MnFe2O4 by a Microwave-Assisted Oxidative Roasting Process

A Novel Method to Synthesize Co/Fe3O4 Nanocomposites with Optimal Magnetic and Microwave Performance

Calcination effects on the crystal structure and magnetic properties of CoFe2O4 nanopowders synthesized by the coprecipitation method

Microwave Sol-Gel Synthesis of Co, Ni, Cu, Mn Ferrites and İnvestigation of Their Activity in the Oxidation Reaction of Carbon Monoxide

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route

Characteristic and Mechanistic Study of Enhanced Carbon-Based Synfuel from Biomass and Coal by Magnetite Additive for Synergistic Co-Carbonization Technology.

Synthesis and characterization of CoFe2O4 ferrite nanoparticles obtained by an electrochemical method

Nanophased CoFe2O4 Prepared by Combustion Method

Temperature-dependence structural, morphological and magnetic properties of cobalt-cadmium ferrite nanoparticles: supported by theoretical study

Preparation and Magnetic Properties of Cobalt-Doped FeMn2O4 Spinel Nanoparticles

Synthesis-Dependent Structural and Magnetic Properties of Monodomain Cobalt Ferrite Nanoparticles